PA6

PA6 Ultramid® B3EG10 BASF GERMANY

270

Unit Price:US$ 3,537 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜Oil resistant
Application Areas:Thin walled components｜Plastic accessories｜Shell
Color:--
Grade:Enhanced level

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	100 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	90 kJ/m²

flammability	Test Method	Test Result
Flammability level	UL 94	HB
Halogen Content	Internal Method	< 100 mg/kg
Polymer Abbreviation		PA6-GF50

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	320 Mpa
Bending modulus		ISO 178	15000 Mpa
Tensile creep modulus	1000 hr	ISO 899-1	7400 Mpa
Tensile strain	Break	ISO 527-2	3.0 %
tensile strength	Break	ISO 527-2	235 Mpa
Tensile modulus		ISO 527-2	16000 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			80 °C
drying time			4.0 hr
Suggested maximum moisture content			0.15 %
Hopper temperature			80 °C
Temperature at the rear of the barrel			270 °C
Residence Time			< 10.0 min
Screw speed			< 18 m/min
Temperature in the middle of the barrel			280 °C
Temperature at the front of the material cylinder			290 °C
Spray nozzle temperature			290 °C
Processing (melt) temperature			280 to 300 °C
Mold temperature			80 to 90 °C

thermal performance	Test Condition	Test Method	Test Result
Maximum operating temperature	短周期操作		200 °C
Linear coefficient of thermal expansion	Flow : 23 to 80°C	ISO 11359-2	1.0E-5 到 1.5E-5 cm/cm/°C
Melting temperature		ISO 11357-3	220 °C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	215 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	220 °C
thermal conductivity		DIN 52612	0.38 W/m/K
specific heat			1300 J/kg/°C
Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	5.0E-5 到 6.0E-5 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Stickiness	96% H2SO4	ISO 307	135 cm³/g
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	1.3 to 1.7 %
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	4.5 to 5.1 %
Melt Volume Flow Rate (MVR)	275°C/5.0 kg	ISO 1133	15.0 cm3/10min
Apparent density			0.70 g/cm³
Mold Shrinkage - Constrained			0.30 %

Electrical performance	Test Condition	Test Method	Test Result
Relative permittivity	1 MHz	IEC 60250	4.20
Volume resistivity		IEC 60093	1.0E+15 ohms·cm
Surface resistivity		IEC 60093	1.0E+10 ohms
Dissipation factor	1 MHz	IEC 60250	0.014
Compared to the anti leakage trace index	Solution A	IEC 60112	PLC 1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.