Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 B3EG10 BASF GERMANY
Ultramid®
Thin walled components、Plastic accessories、Shell
High mobility、Oil resistant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/B3EG10 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 100 kJ/m² |
| -30°C | ISO 179/1eU | 90 kJ/m² |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/B3EG10 |
|---|---|---|---|
| Tensile creep modulus | 1000 hr | ISO 899-1 | 7400 Mpa |
| Tensile modulus | ISO 527-2 | 16000 Mpa | |
| bending strength | ISO 178 | 320 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.0 % |
| Flexural modulus | ISO 178 | 15000 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 235 Mpa |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/B3EG10 |
|---|---|---|---|
| Dissipation Factor | 1 MHz | IEC 60250 | 0.014 |
| Volume resistivity | IEC 60093 | 1.0E+15 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案 A | IEC 60112 | PLC 1 |
| relative permittivity | 1 MHz | IEC 60250 | 4.20 |
| Surface Resistivity | IEC 60093 | 1.0E+10 ohms |
| flammability | Test Condition | Test Method | BASF GERMANY/B3EG10 |
|---|---|---|---|
| Halogen Content | 内部方法 | < 100 mg/kg | |
| Flammability level | UL 94 | HB | |
| Polymer Abbreviation | PA6-GF50 |
| physical property | Test Condition | Test Method | BASF GERMANY/B3EG10 |
|---|---|---|---|
| Apparent density | 0.70 g/cm³ | ||
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 1.3 to 1.7 % |
| Mold Shrinkage - Constrained | 0.30 % | ||
| viscosity number | 96% H2SO4 | ISO 307 | 135 cm³/g |
| Melt volume flow rate | 275°C/5.0 kg | ISO 1133 | 15.0 cm3/10min |
| Water absorption rate | 饱和, 23°C | ISO 62 | 4.5 to 5.1 % |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/B3EG10 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 220 °C | |
| thermal conductivity | DIN 52612 | 0.38 W/m/K | |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 220 °C |
| Linear coefficient of thermal expansion | 横向 : 23 到 80°C | ISO 11359-2 | 5.0E-5 到 6.0E-5 cm/cm/°C |
| 流动 : 23 到 80°C | ISO 11359-2 | 1.0E-5 到 1.5E-5 cm/cm/°C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 215 °C |
| specific heat | 1300 J/kg/°C | ||
| maximum service temperature | 短周期操作 | 200 °C |
| injection | Test Condition | Test Method | BASF GERMANY/B3EG10 |
|---|---|---|---|
| drying time | 4.0 hr | ||
| Suggested maximum moisture content | 0.15 % | ||
| Temperature in the middle of the barrel | 280 °C | ||
| Temperature at the rear of the barrel | 270 °C | ||
| Processing (melt) temperature | 280 to 300 °C | ||
| Hopper temperature | 80 °C | ||
| drying temperature | 80 °C | ||
| Temperature at the front of the material cylinder | 290 °C | ||
| screw speed | < 18 m/min | ||
| Temperature | 80 to 90 °C | ||
| Spray nozzle temperature | 290 °C | ||
| Residence Time | < 10.0 min |