PPO NORYL™ V0150B-701 SABIC INNOVATIVE SHANGHAI

530

Unit Price:US$ 3,950 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
45MT
Delivery Terms:
FOB
Port of Loading :
Shanghai port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜High mobility｜Glass fiber reinforced
Application Areas:Automotive interior parts｜Electrical applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C, Total Energy	ASTM D3763	50.0	J
Charpy Notched Impact Strength	23°C	ISO 179/1eA	14	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	5.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning wire flammability index	1.0 mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	1.0 mm	IEC 60695-2-13	775	°C
UL flame retardant rating	1.5 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	2.0 mm	UL 94	5VA
Extreme Oxygen Index		ISO 4589-2	32	%
Hot filament ignition temperature	2.0 mm	IEC 60695-2-13	775	°C
Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	775	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	Internal Method	35.0	mg
bending strength	Yield, 50.0 mm Span5	ASTM D790	105	Mpa
bending strength	bending strength	--6,7	ISO 178	110	Mpa
Bending modulus	--6	ISO 178	2400	Mpa
Bending modulus	Bending modulus	50.0 mm Span5	ASTM D790	2550	Mpa
elongation	Break	ISO 527-2/50	10	%
	elongation	Break4	ASTM D638	7.0	%
		elongation	Yield	ISO 527-2/50	4.0	%
		elongation	elongation	Yield4	ASTM D638	5.0	%
tensile strength	Break	ISO 527-2/50	55.0	Mpa
	tensile strength	Break4	ASTM D638	60.0	Mpa
		tensile strength	Yield	ISO 527-2/50	70.0	Mpa
		tensile strength	tensile strength	Yield4	ASTM D638	70.0	Mpa
Tensile modulus	--	ISO 527-2/1	2500	Mpa
Tensile modulus	Tensile modulus	--3	ASTM D638	2500	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			110 to 120	°C
drying time			2.0 to 3.0	hr
Hopper temperature			80 to 100	°C
Temperature at the rear of the barrel			260 to 280	°C
Temperature in the middle of the barrel			280 to 300	°C
Temperature at the front of the material cylinder			300 to 320	°C
Spray nozzle temperature			280 to 300	°C
Processing (melt) temperature			300 to 320	°C
Mold temperature			100 to 130	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span10	ISO 75-2/Be	140	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	135	°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Ball Pressure Test	Ball Pressure Test	140°C12	IEC 60695-10-2	通过
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span10	ISO 75-2/Ae	130	°C
Vicat softening temperature	--	ASTM D152511	155	°C
	Vicat softening temperature	--	ISO 306/A50	160	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	145	°C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.5E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Flow : 23 to 80°C	ISO 11359-2	7.0E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.5E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	9.0E-5	cm/cm/°C
thermal conductivity		ISO 8302	0.27	W/m/K
RTI Elec		UL 746	110	°C
RTI Imp		UL 746	105	°C
RTI		UL 746	115	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.060	%
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	0.18	%
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70	%
Shrinkage rate	Shrinkage rate	--2，Flow	Internal Method	0.50 - 0.70	%
Melt Volume Flow Rate (MVR)	300°C/5.0 kg	ISO 1133	10.0	cm3/10min
melt mass-flow rate	280°C/5.0 kg	ASTM D1238	3.5	g/10 min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	> 1.0E+15	ohms
Volume resistivity		IEC 60093	1.0E+15	ohms·cm
Dielectric strength	0.800 mm, in Oil	IEC 60243-1	33	KV/mm
	Dielectric strength	1.60 mm, in Oil	IEC 60243-1	26	KV/mm
	Dielectric strength	Dielectric strength	3.20 mm, in Oil	IEC 60243-1	16	KV/mm
Relative permittivity	50 Hz	IEC 60250	2.80
	Relative permittivity	60 Hz	IEC 60250	2.80
	Relative permittivity	Relative permittivity	1 MHz	IEC 60250	2.70
Dissipation factor	50 Hz	IEC 60250	9.0E-4
	Dissipation factor	60 Hz	IEC 60250	9.0E-4
	Dissipation factor	Dissipation factor	1 MHz	IEC 60250	3.0E-3
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test	H 358/30	ISO 2039-1	113	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Dongguan Junlong	US$ 4610 /MT
Dongguan Puwei	US$ 5650 /MT
Guangzhou HuShang Chemical	US$ 6290 /MT

Supplier Join

Get App

Top

PPO NORYL™ V0150B-701 SABIC INNOVATIVE SHANGHAI

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index