Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO V0150B-701 SABIC INNOVATIVE SHANGHAI
NORYL™ 
Automotive interior parts、Electrical applications
High temperature resistan、High mobility、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/V0150B-701
Charpy Notched Impact Strength23°CISO 179/1eA14 kJ/m²
-30°CISO 179/1eA5.0 kJ/m²
Dart impact23°C, Total EnergyASTM D376350.0 J
hardnessTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/V0150B-701
ball-indentation hardnessH 358/30ISO 2039-1113 Mpa
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/V0150B-701
tensile strength 屈服4ASTM D63870.0 Mpa
elongation断裂4ASTM D6387.0 %
Tensile modulus--3ASTM D6382500 Mpa
Flexural modulus50.0 mm 跨距5ASTM D7902550 Mpa
elongation断裂ISO 527-2/5010 %
bending strength--6,7ISO 178110 Mpa
Taber abraser1000 Cycles, 1000 g, CS-17 转轮内部方法35.0 mg
Flexural modulus--6ISO 1782400 Mpa
bending strength屈服, 50.0 mm 跨距5ASTM D790105 Mpa
tensile strength 断裂ISO 527-2/5055.0 Mpa
屈服ISO 527-2/5070.0 Mpa
elongation屈服ISO 527-2/504.0 %
屈服4ASTM D6385.0 %
tensile strength 断裂4ASTM D63860.0 Mpa
Tensile modulus--ISO 527-2/12500 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/V0150B-701
dielectric strength1.60 mm, 在油中IEC 60243-126 KV/mm
relative permittivity50 HzIEC 602502.80
Dissipation Factor1 MHzIEC 602503.0E-3
Volume resistivityIEC 600931.0E+15 ohms·cm
dielectric strength0.800 mm, 在油中IEC 60243-133 KV/mm
Dissipation Factor60 HzIEC 602509.0E-4
relative permittivity1 MHzIEC 602502.70
Dissipation Factor50 HzIEC 602509.0E-4
Surface ResistivityIEC 60093> 1.0E+15 ohms
dielectric strength3.20 mm, 在油中IEC 60243-116 KV/mm
relative permittivity60 HzIEC 602502.80
Compared to the Leakage Tracking Index (CTI)IEC 60112 V
flammabilityTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/V0150B-701
Hot filament ignition temperature2.0 mmIEC 60695-2-13775 °C
3.0 mmIEC 60695-2-13775 °C
UL flame retardant rating2.0 mmUL 945VA
Hot filament ignition temperature1.0 mmIEC 60695-2-13775 °C
UL flame retardant rating1.5 mmUL 94V-0
Burning wire flammability index1.0 mmIEC 60695-2-12960 °C
Limiting Oxygen IndexISO 4589-232 %
physical property Test ConditionTest MethodSABIC INNOVATIVE SHANGHAI/V0150B-701
melt mass-flow rate280°C/5.0 kgASTM D12383.5 g/10 min
Water absorption rate平衡, 23°C, 50% RHISO 620.060 %
Melt volume flow rate300°C/5.0 kgISO 113310.0 cm3/10min
Shrinkage rate--2，Flow内部方法0.50 - 0.70 %
Water absorption rate饱和, 23°CISO 620.18 %
Shrinkage rate3.20 mm，Flow内部方法0.50 - 0.70 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/V0150B-701
Linear coefficient of thermal expansion流动 : -40 到 40°CASTM E8317.5E-5 cm/cm/°C
vicat--ASTM D152511155 °C
Linear coefficient of thermal expansion横向 : 23 到 80°CISO 11359-29.0E-5 cm/cm/°C
流动 : 23 到 80°CISO 11359-27.0E-5 cm/cm/°C
Heat distortion temperature1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距10，HDTISO 75-2/Ae130 °C
ball-indentation hardness123 到 127°CIEC 60695-10-2通过
RTIUL 746115 °C
thermal conductivityISO 83020.27 W/m/K
vicat--ISO 306/A50160 °C
Heat distortion temperature0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距10，HDTISO 75-2/Be140 °C
vicat--ISO 306/B50145 °C
ball-indentation hardness140°C12IEC 60695-10-2通过
RTI ImpUL 746105 °C
Linear coefficient of thermal expansion横向 : -40 到 40°CASTM E8317.5E-5 cm/cm/°C
Heat distortion temperature1.8 MPa, 未退火, 3.20 mm，HDTASTM D648135 °C
RTI ElecUL 746110 °C
injectionTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/V0150B-701
drying time2.0 to 3.0 hr
Temperature in the middle of the barrel280 to 300 °C
Temperature at the rear of the barrel260 to 280 °C
Processing (melt) temperature300 to 320 °C
Hopper temperature80 to 100 °C
drying temperature110 to 120 °C
Temperature at the front of the material cylinder300 to 320 °C
Temperature100 to 130 °C
Spray nozzle temperature280 to 300 °C