PA66

PA66 Zytel®  PC310 NC010 DUPONT USA

184
  • Unit Price:US$ 6,877 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    52.3MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Non enhanced｜lubrication
  • Application Areas:Electronic and Electrical Applications｜Medical field｜furniture
  • Color:--
  • Grade:--

Technical Data Sheet

Filling analysisTest ConditionTest MethodTest Result
Melt density0.970 g/cm³
Top out temperature190 °C
Specific Heat Capacity of Melt2790 J/kg/°C
Thermal Conductivity of Melt0.16 W/m/K
impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Impact strength of simply supported beam without notch-30°CISO 179/1eU400 kJ/m²
flammabilityTest ConditionTest MethodTest Result
UL flame retardant ratingUL 94V-2
UL flame retardant ratingUL 94V-2
Extreme Oxygen IndexISO 4589-228 %
mechanical propertiesTest ConditionTest MethodTest Result
Bending modulusISO 1782800 Mpa
Tensile creep modulus1000 hrISO 899-1-- Mpa
Tensile creep modulus1 hrISO 899-1-- Mpa
Nominal tensile fracture strainISO 527-225 %
Tensile strainYieldISO 527-24.5 %
tensile strengthYieldISO 527-282.0 Mpa
Tensile modulusISO 527-23100 Mpa
injectionTest ConditionTest MethodTest Result
Maximum Screw Tangential Speed24 m/min
drying temperature80 °C
Drying time - hot air dryer2.0 to 4.0 hr
Suggested maximum moisture content0.20 %
Processing (melt) temperature280 to 300 °C
Melt Temperature, Optimum290 °C
Mold temperature50 to 90 °C
Mold Temperature, Optimum70 °C
Maintain pressure50.0 to 100 Mpa
Maintain pressureDrying Recommendedyes
Hold Pressure Time4.00 s/mm
thermal performanceTest ConditionTest MethodTest Result
Effective thermal diffusivity coefficient5.00E-8 m²/s
Linear coefficient of thermal expansionAcross FlowISO 11359-21.1E-4 cm/cm/°C
Linear coefficient of thermal expansionFlowISO 11359-21.0E-4 cm/cm/°C
Melting temperatureISO 11357-3262 °C
Vicat softening temperatureISO 306/B50240 °C
Glass transition temperatureISO 11357-260.0 °C
Hot deformation temperature1.8 MPa, UnannealedISO 75-2/A70.0 °C
Hot deformation temperature0.45 MPa, UnannealedISO 75-2/B200 °C
Physical propertiesTest ConditionTest MethodTest Result
StickinessISO 307150 cm³/g
Water absorption rateEquilibrium, 23°C, 2.00 mm, 50% RHISO 622.6 %
Water absorption rateSaturation, 23°C, 2.00 mmISO 628.5 %
Shrinkage rateFlowISO 294-41.4 %
Shrinkage rate横向FlowISO 294-41.4 %
Electrical performanceTest ConditionTest MethodTest Result
Surface resistivityIEC 62631-3-2-- ohms
Volume resistivityIEC 62631-3-11.0E+12 ohms·m
Dielectric strengthIEC 60243-132 KV/mm
Relative permittivity1 MHzIEC 62631-2-13.50
Relative permittivity100 HzIEC 62631-2-13.80
Dissipation factor100 HzIEC 62631-2-18.0E-3
Dissipation factor1 MHzIEC 62631-2-10.018
Compared to the anti leakage trace indexIEC 60112PLC 0
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR -SaleISO 2039-2121
Rockwell hardnessM -SaleISO 2039-279
filmTest ConditionTest MethodTest Result
elongationYield， MDISO 527-34.5 %
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.