Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 PC310 NC010 DUPONT USA
Zytel®
Electronic and Electrical Applications,Medical field,furniture
Non enhanced,lubrication
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | DUPONT USA/PC310 NC010 |
|---|---|---|---|
| Rockwell hardness | M 计秤 | ISO 2039-2 | 79 |
| R 计秤 | ISO 2039-2 | 121 |
| film | Test Condition | Test Method | DUPONT USA/PC310 NC010 |
|---|---|---|---|
| elongation | 屈服， MD | ISO 527-3 | 4.5 % |
| thermal performance | Test Condition | Test Method | DUPONT USA/PC310 NC010 |
|---|---|---|---|
| Effective thermal diffusivity coefficient | 5.00E-8 m²/s | ||
| Glass transition temperature | ISO 11357-2 | 60.0 °C | |
| Hot deformation temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 200 °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 70.0 °C | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 1.0E-4 cm/cm/°C |
| 横向 | ISO 11359-2 | 1.1E-4 cm/cm/°C | |
| Melting temperature | ISO 11357-3 | 262 °C | |
| Vicat softening temperature | ISO 306/B50 | 240 °C |
| mechanical properties | Test Condition | Test Method | DUPONT USA/PC310 NC010 |
|---|---|---|---|
| Bending modulus | ISO 178 | 2800 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 25 % | |
| Tensile creep modulus | 1 hr | ISO 899-1 | -- Mpa |
| 1000 hr | ISO 899-1 | -- Mpa | |
| Tensile modulus | ISO 527-2 | 3100 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 4.5 % |
| tensile strength | 屈服 | ISO 527-2 | 82.0 Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT USA/PC310 NC010 |
|---|---|---|---|
| Compared to the anti leakage trace index | IEC 60112 | PLC 0 | |
| Dielectric strength | IEC 60243-1 | 32 KV/mm | |
| Dissipation factor | 1 MHz | IEC 62631-2-1 | 0.018 |
| 100 Hz | IEC 62631-2-1 | 8.0E-3 | |
| Relative permittivity | 1 MHz | IEC 62631-2-1 | 3.50 |
| 100 Hz | IEC 62631-2-1 | 3.80 | |
| Surface resistivity | IEC 62631-3-2 | -- ohms | |
| Volume resistivity | IEC 62631-3-1 | 1.0E+12 ohms·m |
| Physical properties | Test Condition | Test Method | DUPONT USA/PC310 NC010 |
|---|---|---|---|
| Shrinkage rate | 横向流量 | ISO 294-4 | 1.4 % |
| 流量 | ISO 294-4 | 1.4 % | |
| Stickiness | ISO 307 | 150 cm³/g | |
| Water absorption rate | 饱和, 23°C, 2.00 mm | ISO 62 | 8.5 % |
| 平衡, 23°C, 2.00 mm, 50% RH | ISO 62 | 2.6 % |
| impact performance | Test Condition | Test Method | DUPONT USA/PC310 NC010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 400 kJ/m² |
| 23°C | ISO 179/1eU | 无断裂 |
| flammability | Test Condition | Test Method | DUPONT USA/PC310 NC010 |
|---|---|---|---|
| Extreme Oxygen Index | ISO 4589-2 | 28 % | |
| UL flame retardant rating | UL 94 | V-2 |
| Filling analysis | Test Condition | Test Method | DUPONT USA/PC310 NC010 |
|---|---|---|---|
| Melt density | 0.970 g/cm³ | ||
| Specific Heat Capacity of Melt | 2790 J/kg/°C | ||
| Thermal Conductivity of Melt | 0.16 W/m/K | ||
| Top out temperature | 190 °C |
| injection | Test Condition | Test Method | DUPONT USA/PC310 NC010 |
|---|---|---|---|
| drying temperature | 80 °C | ||
| Drying time - hot air dryer | 2.0 to 4.0 hr | ||
| Hold Pressure Time | 4.00 s/mm | ||
| Maintain pressure | Drying Recommended | yes | |
| 50.0 to 100 Mpa | |||
| Maximum Screw Tangential Speed | 24 m/min | ||
| Melt Temperature, Optimum | 290 °C | ||
| Mold temperature | 50 to 90 °C | ||
| Mold Temperature, Optimum | 70 °C | ||
| Processing (melt) temperature | 280 to 300 °C | ||
| Suggested maximum moisture content | 0.20 % |