thermal performance	Test Method	Test Result
Combustibility (rate)	UL 94	V-2
Continuous use temperature	°C	110to220
8.0Mpa, Not annealed	°C	65to220
1.8MPa, Not annealed	°C	230to250
horizontal	mm/mm/°C	68.6E-5-127.0E-5
flow	mm/mm/°C	142.2E-5-203.2E-5
melting temperature	°C	260

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23℃	kJ/m²	11.143to19.964

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	1.6
Water absorption rate		ASTM D570/ISO 62	0.7-1.1 %
Saturation, 23 ℃		%	3.5to5.0
Balance, 23 ℃, 50% RH		%	1.2to1.5
shrinkage rate	23℃	%	0.10-0.31

Electrical performance	Test Condition	Test Method	Test Result
dielectric strength	23℃	V/mil	840
volume resistivity	23℃	ohms·cm	1.0E+12-1.0E+14

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638/ISO 527	16000/12000 kg/cm²(MPa)[Lb/in²]
tensile strength	断裂,23℃		144.83to292.41 MPa
Tensile modulus	23℃		8206.9to28000.0 MPa
Tensile strain	断裂,23℃	%	1.9to3.1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.