Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PA66 A3X2G10 BASF GERMANY
Ultramid®
Laptop case
High mobility,heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | BASF GERMANY/A3X2G10 |
---|---|---|---|
Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 11.143to19.964 |
hardness | Test Condition | Test Method | BASF GERMANY/A3X2G10 |
---|---|---|---|
ball-indentation hardness | 222.76to370.34 MPa |
Mechanical properties | Test Condition | Test Method | BASF GERMANY/A3X2G10 |
---|---|---|---|
Tensile strain | 断裂,23℃ | % | 1.9to3.1 |
Tensile modulus | ASTM D638/ISO 527 | 16000/12000 kg/cm²(MPa)[Lb/in²] | |
tensile strength | 断裂,23℃ | 144.83to292.41 MPa | |
Tensile modulus | 23℃ | 8206.9to28000.0 MPa |
Electrical performance | Test Condition | Test Method | BASF GERMANY/A3X2G10 |
---|---|---|---|
dielectric strength | 23℃ | V/mil | 840 |
Volume resistivity | 23℃ | ohms·cm | 1.0E+12-1.0E+14 |
Physical properties | Test Condition | Test Method | BASF GERMANY/A3X2G10 |
---|---|---|---|
density | ASTM D792/ISO 1183 | 1.6 | |
Water absorption rate | ASTM D570/ISO 62 | 0.7-1.1 % |
physical property | Test Condition | Test Method | BASF GERMANY/A3X2G10 |
---|---|---|---|
Balance, 23 ℃, 50% RH | % | 1.2to1.5 | |
Saturation, 23 ℃ | % | 3.5to5.0 | |
Shrinkage rate | 23℃ | % | 0.10-0.31 |
Thermal performance | Test Condition | Test Method | BASF GERMANY/A3X2G10 |
---|---|---|---|
Combustibility (rate) | UL 94 | V-2 | |
8.0Mpa, Not annealed | °C | 65to220 | |
Continuous use temperature | °C | 110to220 | |
flow | mm/mm/°C | 142.2E-5-203.2E-5 | |
1.8MPa, Not annealed | °C | 230to250 | |
horizontal | mm/mm/°C | 68.6E-5-127.0E-5 | |
melting temperature | °C | 260 |