PPS

PPS Susteel® GS-40 TOSOH JAPAN

299

Unit Price:US$ 9,707 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:enhance｜Glass fiber reinforced
Application Areas:Fiber grade
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			韧性良好
Color			黑色
purpose			注射型

machinability	Test Condition	Test Method	Test Result
Shrinkage rate	Flow	ASTM D-955	0.3 %
Shrinkage rate	Shrinkage rate	Across Flow	ASTM D-955	0.7 %
Dry conditions			120-150度 2.0-5.0hr
Processing temperature			270-300 °C
Processing temperature	Processing temperature			290-330 °C
Screw speed			100-150 rpm
Mold temperature			135-150 °C
pressure			1.00-20.0 Mpa

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
Elongation at Break		ASTM D-638	1.7 %
tensile strength		ASTM D-638	172 Mpa
Charpy Notched Impact Strength	有Notched	ASTM D-256	74 J/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Unnotched	ASTM D-256	541 J/m
Rockwell hardness		ASTM D-785	122
bending strength		ASTM D-790	275 Mpa
Bending modulus		ASTM D-790	15 GPa
tensile strength	Yield	ISO 527-2	176 Mpa
Tensile strain	Break	ISO 527-2	1.5 %
Bending modulus		ISO 178	14700 Mpa
bending strength		ISO 178	275 Mpa
Tensile Weld Strength		Internal Method	60.0 Mpa
Impact strength of cantilever beam gap		ASTM D256/ISO 179	82 kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	1.5 %
tensile strength		ASTM D638/ISO 527	176 kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	14700 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	275 kg/cm²(MPa)[Lb/in²]

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion		自定标准	2.2
UL flame retardant rating		UL 94	V-0
Hot deformation temperature	1.82MPa	ASTM D-648	＞260 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	>260 °C
Melting temperature		Internal Method	285 °C
Hot deformation temperature	HDT	ASTM D648/ISO 75	260 ℃（℉）
Melting temperature			285 ℃（℉）

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD	ISO 294-4	0.80 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.30 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	<0.020 %
density		ASTM D792/ISO 1183	1.64
Shrinkage rate		ASTM D955	0.3-0.8 %
Water absorption rate		ASTM D570/ISO 62	0.02 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		ASTM D-257	4×1016 Ω.cm
Dielectric constant	1MHz	ASTM D-150	3.9
Dissipation factor	1MHz	ASTM D-150	0.0014
Dielectric strength		ASTM D-149	16 KV/mm
thermal conductivity		自定标准	0.27 W/m.K
Volume resistivity		IEC 60093	1E+17 ohms·cm
Dielectric strength		IEC 60243-1	16 KV/mm
Dielectric constant	1MHz	IEC 60250	3.90
Dissipation factor	1MHz	IEC 60250	1.4E-03
Compared to the anti leakage trace index	CTI	UL 746	PLC 4
Compared to the anti leakage trace index	Compared to the anti leakage trace index		IEC 60112	PLC 4
Dielectric constant		ASTM D150/IEC 60250	3.90

Supplementary Information	Test Condition	Test Method	Test Result
BarFlowLength		Internal Method	175 mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.