PC Makrolon® 6267 X COVESTRO SHANGHAI

263

Unit Price:US$ 3,622 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
17MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Low viscosity｜Flame retardant
Application Areas:Home appliance components｜Bottle cap｜Electronic and electrical components｜Lighting applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Multi axis Instrumented Peak Impact Force	23°C	ISO 6603-2	5000 N
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	23°C,Partial Break	ISO 7391	60 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C,Complete Break	ISO 7391	12 kJ/m²
Multi axis Instrumented Peak Impact Force	-30°C	ISO 6603-2	5900 N
Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	50.0 J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	-30°C	ISO 6603-2	55.0 J
Impact strength of cantilever beam gap	23°C,Partial Break	ISO 7391	15 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C,Complete Break	ISO 7391	11 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	V-0
Burning wire flammability index	0.75mm	IEC 60695-2-12	960 °C
	Burning wire flammability index	1.5mm	IEC 60695-2-12	960 °C
	Burning wire flammability index	Burning wire flammability index	3.0mm	IEC 60695-2-12	960 °C
Extreme Oxygen Index		ISO 4589-2	36 %
ApplicationofFlamefromSmallBurner MethodKandF	2.00mm	DIN 53438-1,-3	K1.F1
FlashIgnitionTemperature		ASTM D1929	460 °C
UL flame retardant rating	1.50mm	IEC 60695-11-5	2.0 min
	UL flame retardant rating	2.00mm	IEC 60695-11-5	2.0 min
		UL flame retardant rating	3.00mm	IEC 60695-11-5	2.0 min
			UL flame retardant rating	1.50mm	IEC 60695-11-5	2.0 min
				UL flame retardant rating	2.00mm	IEC 60695-11-5	2.0 min
				UL flame retardant rating	UL flame retardant rating	3.00mm	IEC 60695-11-5	2.0 min
SelfIgnition		ASTM D1929	530 °C
Burning rate - US-FMVSS	>1.00mm	ISO 3795	passed

mechanical properties	Test Condition	Test Method	Test Result
Bending strain	23°C	ISO 178	6.9 %
tensile strength	Break,23°C	ISO 527-2/50	65.0 Mpa
Tensile modulus	23°C	ISO 527-2/1	2450 Mpa
tensile strength	Yield,23°C	ISO 527-2/50	67.0 Mpa
bending strength	3.5%Strain,23°C	ISO 178	74.0 Mpa
Tensile strain	Yield,23°C	ISO 527-2/50	6.0 %
Tensile strain	Tensile strain	Break,23°C	ISO 527-2/50	120 %
Nominal tensile fracture strain	23°C	ISO 527-2/50	>50 %
Bending modulus	23°C	ISO 178	2400 Mpa
bending strength	23°C	ISO 178	97.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature	--	ISO 306/B120	145 °C
Ball Pressure Test	135°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	MD:23to55°C	ISO 11359-2	6.5E-05 cm/cm/°C
Vicat softening temperature	--	ISO 306/B50	144 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	122 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	134 °C
RTI	1.5mm	UL 746	125 °C
RTI Imp	1.5mm	UL 746	115 °C
Linear coefficient of thermal expansion	TD:23to55°C	ISO 11359-2	6.5E-05 cm/cm/°C
thermal conductivity	23°C	ISO 8302	0.20 W/m/K
RTI Elec	1.5mm	UL 746	125 °C

Physical properties	Test Condition	Test Method	Test Result
Apparent density		ISO 60	0.64 g/cm³
melt mass-flow rate	300°C/1.2kg	ISO 1133	20 g/10min
Water absorption rate	Saturation,23°C	ISO 62	0.30 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.12 %
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	19.0 cm3/10min
Shrinkage rate	TD	ISO 2577	0.50-0.70 %
	Shrinkage rate	MD	ISO 2577	0.50-0.70 %
		Shrinkage rate	TD:2.00mm4	ISO 294-4	0.65 %
		Shrinkage rate	Shrinkage rate	MD:2.00mm4	ISO 294-4	0.65 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	SolutionA	IEC 60112	V
Dissipation factor	23°C,1MHz	IEC 60250	9E-03
Dissipation factor	Dissipation factor	23°C,100Hz	IEC 60250	8E-04
Relative permittivity	23°C,1MHz	IEC 60250	3.00
Relative permittivity	Relative permittivity	23°C,100Hz	IEC 60250	3.10
Dielectric strength	23°C,1.00mm	IEC 60243-1	34 KV/mm
Volume resistivity	23°C	IEC 60093	1E+16 ohms·cm
Surface resistivity		IEC 60093	1E+16 ohms
Compared to the anti leakage trace index	SolutionB	IEC 60112	V

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test		ISO 2039-1	116 Mpa

Supplementary Information	Test Condition	Test Method	Test Result
Electrolytic corrosion	23°C	IEC 60426	A1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC Makrolon® 6267 X COVESTRO SHANGHAI

Material Description

Technical Data Sheet Compare

Technical Data Sheet