Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 6267 X COVESTRO SHANGHAI
Makrolon® 
Home appliance components,Bottle cap,Electronic and electrical components,Lighting applications
Low viscosity,Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodCOVESTRO SHANGHAI/6267 X
Ball Pressure TestISO 2039-1116 Mpa
Supplementary InformationTest ConditionTest MethodCOVESTRO SHANGHAI/6267 X
Electrolytic corrosion23°CIEC 60426A1
thermal performanceTest ConditionTest MethodCOVESTRO SHANGHAI/6267 X
Ball Pressure Test135°CIEC 60695-10-2通过
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B134 °C
1.8MPa,UnannealedISO 75-2/A122 °C
Linear coefficient of thermal expansionTD:23to55°CISO 11359-26.5E-05 cm/cm/°C
MD:23to55°CISO 11359-26.5E-05 cm/cm/°C
RTI1.5mmUL 746125 °C
RTI Elec1.5mmUL 746125 °C
RTI Imp1.5mmUL 746115 °C
thermal conductivity23°CISO 83020.20 W/m/K
Vicat softening temperature--ISO 306/B120145 °C
--ISO 306/B50144 °C
mechanical propertiesTest ConditionTest MethodCOVESTRO SHANGHAI/6267 X
Bending modulus23°CISO 1782400 Mpa
Bending strain23°CISO 1786.9 %
bending strength23°CISO 17897.0 Mpa
3.5%Strain,23°CISO 17874.0 Mpa
Nominal tensile fracture strain23°CISO 527-2/50>50 %
Tensile modulus23°CISO 527-2/12450 Mpa
Tensile strainYield,23°CISO 527-2/506.0 %
Break,23°CISO 527-2/50120 %
tensile strengthBreak,23°CISO 527-2/5065.0 Mpa
Yield,23°CISO 527-2/5067.0 Mpa
Electrical performanceTest ConditionTest MethodCOVESTRO SHANGHAI/6267 X
Compared to the anti leakage trace indexSolutionBIEC 60112 V
SolutionAIEC 60112 V
Dielectric strength23°C,1.00mmIEC 60243-134 KV/mm
Dissipation factor23°C,100HzIEC 602508E-04
23°C,1MHzIEC 602509E-03
Relative permittivity23°C,1MHzIEC 602503.00
23°C,100HzIEC 602503.10
Surface resistivityIEC 600931E+16 ohms
Volume resistivity23°CIEC 600931E+16 ohms·cm
Physical propertiesTest ConditionTest MethodCOVESTRO SHANGHAI/6267 X
Apparent densityISO 600.64 g/cm³
melt mass-flow rate300°C/1.2kgISO 113320 g/10min
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 113319.0 cm3/10min
Shrinkage rateMD:2.00mm4ISO 294-40.65 %
TDISO 25770.50-0.70 %
MDISO 25770.50-0.70 %
TD:2.00mm4ISO 294-40.65 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.12 %
Saturation,23°CISO 620.30 %
impact performanceTest ConditionTest MethodCOVESTRO SHANGHAI/6267 X
Charpy Notched Impact Strength23°C,Partial BreakISO 739160 kJ/m²
-30°C,Complete BreakISO 739112 kJ/m²
Impact strength of cantilever beam gap23°C,Partial BreakISO 739115 kJ/m²
-30°C,Complete BreakISO 739111 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
23°CISO 179/1eU无断裂
Multi axis Instrumented Impact Energy-30°CISO 6603-255.0 J
23°CISO 6603-250.0 J
Multi axis Instrumented Peak Impact Force-30°CISO 6603-25900 N
23°CISO 6603-25000 N
flammabilityTest ConditionTest MethodCOVESTRO SHANGHAI/6267 X
ApplicationofFlamefromSmallBurner MethodKandF2.00mmDIN 53438-1,-3K1.F1
Burning rate - US-FMVSS>1.00mmISO 3795passed
Burning wire flammability index3.0mmIEC 60695-2-12960 °C
1.5mmIEC 60695-2-12960 °C
0.75mmIEC 60695-2-12960 °C
Extreme Oxygen IndexISO 4589-236 %
FlashIgnitionTemperatureASTM D1929460 °C
SelfIgnitionASTM D1929530 °C
UL flame retardant rating1.50mmIEC 60695-11-52.0 min
2.00mmIEC 60695-11-52.0 min
3.00mmIEC 60695-11-52.0 min
1.5mmUL 94V-0