POM TENAC™ 3010 ASAHI JAPAN

393

Unit Price:US$ 5,122 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
204MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance｜high molecular weight｜high viscosity
Application Areas:Electrical field｜Electronic field｜Engine parts｜Industrial applications｜Household goods
Color:--
Grade:Impact resistant grade

Material Certification

Technical Data Sheet

Other performance	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

Basic Performance	Test Condition	Test Method	Test Result
density		ASTM D792	1.42 g/cm³
melt mass-flow rate		ASTM D1238	2.8 g/10 min
melt mass-flow rate	melt mass-flow rate	190℃/2.16kg	ISO 1133	2.8 g/10 min
Shrinkage rate	flow	ASTM D955	1.8 - 2.2 %
Shrinkage rate	Shrinkage rate	Across flow	ISO 294-4	1.8 - 2.2 %
Water absorption rate	24hr	ASTM D570	0.20 %
Rockwell hardness	M-Scale	ASTM D785	94

mechanical properties	Test Condition	Test Method	Test Result
tensile strength		ASTM D638	68.0 MPa
elongation	Break	ASTM D638	75 %
bending strength		ASTM D790	98.0 MPa
Taber abraser	1000次	ASTM D1044	13.0 mg
Impact strength of cantilever beam gap		ASTM D256	108 J/m
Tensile modulus		ISO 527-2	3100 MPa
tensile strength		ASTM D638/ISO 527	68 kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	94
Bending modulus		ASTM D790/ISO 178	2740 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	98 kg/cm²(MPa)[Lb/in²]

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	172 °C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	133 °C
		Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	163 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	96.0 °C
Linear coefficient of thermal expansion	flow	ASTM E831	0.00010 cm/cm/°C
Combustibility (rate)		UL 94	HB
Hot deformation temperature	HDT	ASTM D648/ISO 75	133 ℃（℉）

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	1.42
Water absorption rate		ASTM D570/ISO 62	0.2 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

POM TENAC™ 3010 ASAHI JAPAN

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet