Material Description

Material Properties:Low warpage
Application Areas:OA device
Color:--
Grade:--

Technical Data Sheet

machinability	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	3mmt		1.0-1.4	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	-40°C	MPa	185	--
bending strength	bending strength	23°C		155	MPa
Bending modulus	80°C	MPa	2000	--
	Bending modulus	23°C	MPa	5800	3000
	Bending modulus	Bending modulus	-40°C	MPa	6200	--
Tensile strain	Break,80°C	%	5.0	--
Elongation at Break	80℃	D638	8.5	%
	Elongation at Break	23℃	D638	6.0	%
	Elongation at Break	Elongation at Break	-40℃	D638	5.0	%
tensile strength	Yield,80℃	D638	40	Mpa
	tensile strength	Yield,23℃	D638	95	Mpa
		tensile strength	Yield,-40℃	D638	120	Mpa
			tensile strength	23°C	MPa	95.0	70.0
			tensile strength	tensile strength	80°C	MPa	40.0	--
Tensile strain	Break,-40°C	%	3.0	--
Impact strength of cantilever beam gap	23℃	D256	45	J/m
Bending modulus	80℃	D790	2.1	GPa
	Bending modulus	23℃	D790	6.0	GPa
	Bending modulus	Bending modulus	-40℃	D790	6.4	GPa
bending strength	80℃	D790	60	Mpa
	bending strength	23℃	D790	150	Mpa
		bending strength	-40℃	D790	180	Mpa
		bending strength	bending strength	80°C	MPa	65.0	--
tensile strength	-40°C	MPa	120	--
Tensile strain	Break,23°C	%	3.5	5.0
Impact strength of cantilever beam gap		ASTM D256/ISO 179	45	kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	12	%
tensile strength		ASTM D638/ISO 527	85	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	120
Bending modulus		ASTM D790/ISO 178	3500	kg·cm/cm(J/M)ft·lb/in
bending strength		ASTM D790/ISO 178	125	kg·cm/cm(J/M)ft·lb/in
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.86MPa	D648	185	°C
Hot deformation temperature	Hot deformation temperature	0.46Mpa	D648	243	°C
Melting temperature		DSC	265	°C
Hot deformation temperature	0.45MPa,Unannealed	°C	243	--
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	°C	185	--
Melting temperature		°C	265	--
Combustibility (rate)		UL 94	HB
Hot deformation temperature	HDT	ASTM D648/ISO 75	224	℃（℉）
Melting temperature			265	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	23℃,水中	D570	5.1	%
Water absorption rate	Water absorption rate	23℃,24hrs	D570	0.6	%
filler content			40	wt%
Shrinkage rate	MD:3.00mm3	%	0.70-1.0	--
Water absorption rate	23°C,24hr	%	0.60	--
Water absorption rate	Water absorption rate	Saturation,23°C	%	5.1	--
Shrinkage rate	TD:3.00mm2	%	1.0-1.4	--
density		ASTM D792/ISO 1183	1.19
Water absorption rate		ASTM D570/ISO 62	1.1	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D257/IEC 60093	10^13	Ω.cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Sale,23°C		83	--
Rockwell hardness	Rockwell hardness	R-Sale,23°C		120	--

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.