Product Name / Manufacturer / Model

Reference Price

PA66 TORAY JAPAN CM3001R

US$ 4,080 / MT

FOB Guangzhou port, China

Physical properties	Test Condition	Test Method	TORAY JAPAN/CM3001R
Water absorption rate	23℃,24hrs	D570	0.6 %
Water absorption rate		23°C,24hr	%	0.60 --
Shrinkage rate	TD:3.00mm2	%	1.0-1.4 --
density		ASTM D792/ISO 1183	1.19
Water absorption rate		ASTM D570/ISO 62	1.1 %
Shrinkage rate	MD:3.00mm3	%	0.70-1.0 --
Water absorption rate	23℃,水中	D570	5.1 %
Water absorption rate		Saturation,23°C	%	5.1 --
filler content			40 wt%
mechanical properties	Test Condition	Test Method	TORAY JAPAN/CM3001R
Elongation at Break	80℃	D638	8.5 %
bending strength	23°C		155 MPa
Bending modulus	23°C	MPa	5800 3000
tensile strength	Yield,23℃	D638	95 Mpa
bending strength	23℃	D790	150 Mpa
Tensile strain	Break,80°C	%	5.0 --
bending strength		ASTM D790/ISO 178	125 kg·cm/cm(J/M)ft·lb/in
Tensile strain	Break,23°C	%	3.5 5.0
Bending modulus	-40°C	MPa	6200 --
Bending modulus		-40℃	D790	6.4 GPa
Impact strength of cantilever beam gap		ASTM D256/ISO 179	45 kg·cm/cm(J/M)ft·lb/in
Rockwell hardness		ASTM D785	120
Bending modulus	80°C	MPa	2000 --
			ASTM D790/ISO 178	3500 kg·cm/cm(J/M)ft·lb/in
		80℃	D790	2.1 GPa
tensile strength	Yield,-40℃	D638	120 Mpa
tensile strength		80°C	MPa	40.0 --
bending strength	80℃	D790	60 Mpa
Bending modulus	23℃	D790	6.0 GPa
Impact strength of cantilever beam gap	23℃	D256	45 J/m
bending strength	-40℃	D790	180 Mpa
bending strength		80°C	MPa	65.0 --
Elongation at Break	-40℃	D638	5.0 %
Elongation at Break			ASTM D638/ISO 527	12 %
tensile strength	-40°C	MPa	120 --
Tensile strain	Break,-40°C	%	3.0 --
tensile strength	23°C	MPa	95.0 70.0
Elongation at Break	23℃	D638	6.0 %
tensile strength		ASTM D638/ISO 527	85 kg/cm²(MPa)[Lb/in²]
bending strength	-40°C	MPa	185 --
tensile strength	Yield,80℃	D638	40 Mpa
thermal performance	Test Condition	Test Method	TORAY JAPAN/CM3001R
Hot deformation temperature	0.46Mpa	D648	243 °C
		1.8MPa,Unannealed	°C	185 --
		1.86MPa	D648	185 °C
		HDT	ASTM D648/ISO 75	224 ℃（℉）
Melting temperature		°C	265 --
Hot deformation temperature	0.45MPa,Unannealed	°C	243 --
Melting temperature		DSC	265 °C
Combustibility (rate)		UL 94	HB
Melting temperature			265 ℃（℉）
machinability	Test Condition	Test Method	TORAY JAPAN/CM3001R
Shrinkage rate	3mmt		1.0-1.4 %
hardness	Test Condition	Test Method	TORAY JAPAN/CM3001R
Rockwell hardness	R-Sale,23°C		120 --
Rockwell hardness		M-Sale,23°C		83 --
Electrical performance	Test Condition	Test Method	TORAY JAPAN/CM3001R
Volume resistivity		ASTM D257/IEC 60093	10^13 Ω.cm