Material Properties:Low warpage｜Glass fiber reinforced｜Filler: Glass fiber reinforced material｜30% filler by weight
Application Areas:Automotive Applications｜Electrical components｜Laptop case｜Lawn and garden equipment｜Industrial applications｜Parts under the hood of a car｜Vehicle electronics｜Shell｜Valves/valve components｜Metal substitution｜Machine/mechanical components｜currency｜Application in the automotive field｜Industrial components｜bearing｜Fuel pipeline
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result
Water absorption rate		ASTM D570	0.15 %
density		ISO 1183/A	1.34 g/cm³
Shrinkage rate		ASTM D955	0.80 %
Shrinkage rate	Shrinkage rate		ASTM D955	0.50 %

Mechanical properties	Test Condition	Test Method	Test Result
Tensile strain		ISO 527-2	3.3 %
Flexural modulus		ASTM D790	7860 Mpa
Flexural modulus	Flexural modulus		ISO 178	7580 Mpa
bending strength		ISO 178	225 Mpa
bending strength	bending strength		ASTM D790	236 Mpa
tensile strength		ISO 527-2	170 Mpa
tensile strength	tensile strength		ASTM D638	167 Mpa
Tensile modulus		ISO 527-2	9310 Mpa
elongation		ASTM D638	3.2 %

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179/1eA	13 kJ/m²
Impact strength of cantilever beam gap		ASTM D256	130 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256	1400 J/m

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/B	298 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/A	276 °C
melting temperature		ASTM D3418	306 °C
melting temperature	melting temperature		ISO 11357-3	310 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.