PPA AT-6130 HS SOLVAY USA
AMODEL®
Automotive Applications、Electrical components、Laptop case、Lawn and garden equipment、Industrial applications、Parts under the hood of a、Vehicle electronics、Shell、Valves/valve components、Metal substitution、Machine/mechanical compon、currency、Application in the automo、Industrial components、bearing、Fuel pipeline
Low warpage、Glass fiber reinforced、Filler: Glass fiber reinf、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SOLVAY USA/AT-6130 HS |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 13 kJ/m² | |
| Impact strength of cantilever beam gap | ASTM D256 | 1400 J/m |
| Mechanical properties | Test Condition | Test Method | SOLVAY USA/AT-6130 HS |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 9310 Mpa | |
| elongation | 断裂 | ASTM D638 | 3.2 % |
| bending strength | 屈服 | ASTM D790 | 236 Mpa |
| ISO 178 | 225 Mpa | ||
| Tensile strain | 断裂 | ISO 527-2 | 3.3 % |
| Flexural modulus | ISO 178 | 7580 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 170 Mpa |
| 断裂 | ASTM D638 | 167 Mpa | |
| Flexural modulus | ASTM D790 | 7860 Mpa |
| physical property | Test Condition | Test Method | SOLVAY USA/AT-6130 HS |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.50 % |
| Water absorption rate | 24hr | ASTM D570 | 0.15 % |
| density | ISO 1183/A | 1.34 g/cm³ | |
| Shrinkage rate | TD | ASTM D955 | 0.80 % |
| Thermal performance | Test Condition | Test Method | SOLVAY USA/AT-6130 HS |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 310 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 298 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 276 °C | |
| melting temperature | ASTM D3418 | 306 °C |