Material Description
- Material Properties:Chemical resistance｜Recyclable｜Ozone resistant｜Oil resistant｜damping｜Bondable
- Application Areas:Phone｜Kitchen utensils｜Automotive Applications｜Gears｜adhesive｜Phone case｜household electrical appliances｜Home appliance components｜sporting goods｜packing｜hinge｜electrical equipment｜Mirror frame｜Movable hinge｜Application in the automotive field｜Bonding｜Electrical appliances｜Consumer product application field｜Parts under the hood of a car｜Adhesive resin｜Large and small household appliances｜Fatigue relief supplies｜Soft handle
- Color:--
- Grade:Weather resistant grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | 邵氏A,15秒,23°C | ISO 868 | 65 |
| elastomer | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tear strength | 23°C，Across Flow (横向) | ISO 34-1 | 28 kN/m |
| compression set | 23°C,22hr | ASTM D395B | 34 % |
| 70°C,22hr | ASTM D395B | 62 % | |
| 23°C,22hr | ISO 815 | 34 % | |
| 70°C,22hr | ISO 815 | 62 % | |
| Tensile stress | 100%应变,23°C，横向流量 | ASTM D412 | 2.10 Mpa |
| 100%应变,23°C，横向流量 | ISO 37 | 2.10 Mpa | |
| tensile strength | 断裂,23°C，横向流量 | ASTM D412 | 8.00 Mpa |
| Break,23°C | ISO 37 | 8.00 Mpa | |
| elongation | 断裂,23°C，横向 | ASTM D412 | 540 % |
| 断裂,23°C，横向 | ISO 37 | 540 % | |
| tear strength | 23°C，横向流量 | ASTM D624 | 28.0 kN/m |
| aging | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hardness change rate in the air | ShoreA,100°C,672hr | ASTM D573 | -2.0 |
| Shore hardness | ShoreA,100°C,672hr | ISO 188 | -2.0 |
| Changes in air quality | 100°C,168hr | ASTM D573 | -1.1 % |
| 100°C,168hr | ISO 188 | -1.1 % | |
| Volume change in air | 100°C,168hr | ASTM D573 | -1.2 % |
| 100°C,168hr | ISO 188 | -1.2 % | |
| Change rate of tensile strength in air | 23°C,24hr,inIRM903Oil | ASTM D471 | -4.0 % |
| 23°C,168hr,inCascadeDetergent | ASTM D471 | -20 % | |
| 23°C,168hr,inClorox,10% | ASTM D471 | -16 % | |
| 23°C,168hr,inEthanol,50% | ASTM D471 | -65 % | |
| 100°C,168hr | ASTM D573 | 0.0 % | |
| 100°C,168hr | ISO 188 | 0.0 % | |
| Elongation at break | 100°C,168hr | ASTM D573 | -11 % |
| Change rate of tensile strength in air | 23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | -20 % |
| 23°C,168hr,inRelativeHumidity,90% | ASTM D471 | -11 % | |
| 23°C,168hr,inSodiumChloride,15% | ASTM D471 | -18 % | |
| 23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | -22 % | |
| 38°C,168hr,inRelativeHumidity,90% | ASTM D471 | -16 % | |
| 23°C,24hr,inIRM903Oil | ISO 1817 | -4.0 % | |
| 23°C,168hr,inCascadeDetergent | ISO 1817 | -20 % | |
| 23°C,168hr,inClorox,10% | ISO 1817 | -16 % | |
| 23°C,168hr,inEthanol,50% | ISO 1817 | -65 % | |
| 23°C,168hr,inHydrochloricAcid,10% | ISO 1817 | -20 % | |
| Change rate of ultimate elongation in air | 23°C,168hr,inSodiumChloride,15% | ASTM D471 | -6.0 % |
| 23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | -18 % | |
| 38°C,168hr,inRelativeHumidity,90% | ASTM D471 | -9.0 % | |
| Tensile stress change rate | 23°C,24hr,inIRM903Oil，断裂 | ISO 1817 | -4.0-4.0-4.0-4.0-4.0 % |
| 23°C,168hr,inCascadeDetergent，断裂 | ISO 1817 | -7.0 % | |
| 23°C,168hr,inClorox,10%，断裂 | ISO 1817 | -4.0 % | |
| 23°C,168hr,inEthanol,50%，断裂 | ISO 1817 | -66 % | |
| 23°C,168hr,inHydrochloricAcid,10%，断裂 | ISO 1817 | -10 % | |
| 23°C,168hr,inRelativeHumidity,90%，断裂 | ISO 1817 | -10 % | |
| 23°C,168hr,inSodiumChloride,15%，断裂 | ISO 1817 | -6.0 % | |
| 23°C,168hr,inSodiumHydroxide,50%，断裂 | ISO 1817 | -18 % | |
| 38°C,168hr,inRelativeHumidity,90%，断裂 | ISO 1817 | -9.0 % | |
| Hardness change rate in the air | ShoreA,23°C,168hr,inDeionizedWater | ASTM D471 | -1.0 |
| Shore hardness | ShoreA,23°C,168hr,inDeionizedWater | ISO 1817 | -1.0 |
| mass change fraction | 23°C,168hr,inCascadeDetergent | ASTM D471 | 0.10 % |
| 23°C,168hr,inClorox,10% | ASTM D471 | 0.60 % | |
| 23°C,168hr,inEthanol,50% | ASTM D471 | 6.5 % | |
| 23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | 0.40 % | |
| 23°C,168hr,inRelativeHumidity,95% | ASTM D471 | 0.0 % | |
| 23°C,168hr,inSodiumChloride,15% | ASTM D471 | 0.10 % | |
| Change rate of tensile strength in air | 23°C,168hr,inRelativeHumidity,90% | ISO 1817 | -11 % |
| 23°C,168hr,inSodiumChloride,15% | ISO 1817 | -18 % | |
| 23°C,168hr,inSodiumHydroxide,50% | ISO 1817 | -22 % | |
| 38°C,168hr,inRelativeHumidity,90% | ISO 1817 | -16 % | |
| Change rate of ultimate elongation in air | 23°C,24hr,inIRM903Oil | ASTM D471 | -4.0-4.0-4.0-4.0-4.0 % |
| 23°C,168hr,inCascadeDetergent | ASTM D471 | -7.0 % | |
| 23°C,168hr,inClorox,10% | ASTM D471 | -4.0 % | |
| 23°C,168hr,inEthanol,50% | ASTM D471 | -66 % | |
| 23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | -10 % | |
| 23°C,168hr,inRelativeHumidity,90% | ASTM D471 | -10 % | |
| volume change | 23°C,168hr,inCascadeDetergent | ASTM D471 | 0.10 % |
| 23°C,168hr,inClorox,10% | ASTM D471 | 0.60 % | |
| 23°C,168hr,inEthanol,50% | ASTM D471 | 6.8 % | |
| 23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | 0.40 % | |
| 23°C,168hr,inRelativeHumidity,95% | ASTM D471 | 0.0 % | |
| 23°C,168hr,inSodiumChloride,15% | ASTM D471 | 0.60 % | |
| 23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | 0.20 % | |
| 38°C,168hr,inRelativeHumidity,95% | ASTM D471 | 0.60 % | |
| 23°C,168hr,inCascadeDetergent | ISO 1817 | 0.10 % | |
| 23°C,168hr,inClorox,10% | ISO 1817 | 0.60 % | |
| mass change fraction | 23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | 0.10 % |
| 38°C,168hr,inRelativeHumidity,95% | ASTM D471 | 0.60 % | |
| 23.0°C,168hr,inRelativeHumidity,95% | ISO 1817 | 0.0 % | |
| 23.0°C,168hr,inSodiumChloride,15% | ISO 1817 | 0.10 % | |
| 23.0°C,168hr,inCascadeDetergent | ISO 1817 | 0.10 % | |
| 23.0°C,168hr,inSodiumHydroxide,50% | ISO 1817 | 0.10 % | |
| 23.0°C,168hr,inHydrochloricAcid,10% | ISO 1817 | 0.40 % | |
| 38.0°C,168hr,inRelativeHumidity,95% | ISO 1817 | 0.60 % | |
| 23.0°C,168hr,inClorox,10% | ISO 1817 | 0.60 % | |
| 23.0°C,168hr,inEthanol,50% | ISO 1817 | 6.5 % | |
| volume change | 23°C,168hr,inEthanol,50% | ISO 1817 | 6.8 % |
| 23°C,168hr,inHydrochloricAcid,10% | ISO 1817 | 0.40 % | |
| 23°C,168hr,inRelativeHumidity,95% | ISO 1817 | 0.0 % | |
| 23°C,168hr,inSodiumChloride,15% | ISO 1817 | 0.60 % | |
| 23°C,168hr,inSodiumHydroxide,50% | ISO 1817 | 0.20 % | |
| 38°C,168hr,inRelativeHumidity,95% | ISO 1817 | 0.60 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.