Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TPV 291-60B150 CELANESE USA
Santoprene™
Phone、Kitchen utensils、Automotive Applications、Gears、adhesive、Phone case、household electrical appl、Home appliance components、sporting goods、packing、hinge、electrical equipment、Mirror frame、Movable hinge、Application in the automo、Bonding、Electrical appliances、Consumer product applicat、Parts under the hood of a、Adhesive resin、Large and small household、Fatigue relief supplies、Soft handle
Chemical resistance、Recyclable、Ozone resistant、Oil resistant、damping、Bondable
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | CELANESE USA/291-60B150 |
|---|---|---|---|
| Shore hardness | 邵氏A,15秒,23°C | ISO 868 | 65 |
| aging | Test Condition | Test Method | CELANESE USA/291-60B150 |
|---|---|---|---|
| Change rate of ultimate elongation in air | 23°C,168hr,inClorox,10% | ASTM D471 | -4.0 % |
| mass change fraction | 23.0°C,168hr,inEthanol,50% | ISO 1817 | 6.5 % |
| Change rate of ultimate elongation in air | 23°C,24hr,inIRM903Oil | ASTM D471 | -4.0-4.0-4.0-4.0-4.0 % |
| volume change | 23°C,168hr,inRelativeHumidity,95% | ASTM D471 | 0.0 % |
| Shore hardness | ShoreA,100°C,672hr | ISO 188 | -2.0 |
| Change rate of tensile strength in air | 23°C,168hr,inHydrochloricAcid,10% | ISO 1817 | -20 % |
| Volume change in air | 100°C,168hr | ASTM D573 | -1.2 % |
| volume change | 23°C,168hr,inClorox,10% | ISO 1817 | 0.60 % |
| Tensile stress change rate | 23°C,24hr,inIRM903Oil，断裂 | ISO 1817 | -4.0-4.0-4.0-4.0-4.0 % |
| Change rate of tensile strength in air | 23°C,168hr,inRelativeHumidity,90% | ISO 1817 | -11 % |
| Volume change in air | 100°C,168hr | ISO 188 | -1.2 % |
| Change rate of ultimate elongation in air | 23°C,168hr,inRelativeHumidity,90% | ASTM D471 | -10 % |
| 23°C,168hr,inSodiumChloride,15% | ASTM D471 | -6.0 % | |
| mass change fraction | 38.0°C,168hr,inRelativeHumidity,95% | ISO 1817 | 0.60 % |
| Change rate of tensile strength in air | 23°C,168hr,inSodiumChloride,15% | ASTM D471 | -18 % |
| Tensile stress change rate | 23°C,168hr,inRelativeHumidity,90%，断裂 | ISO 1817 | -10 % |
| mass change fraction | 23°C,168hr,inCascadeDetergent | ASTM D471 | 0.10 % |
| 23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | 0.10 % | |
| volume change | 23°C,168hr,inSodiumHydroxide,50% | ISO 1817 | 0.20 % |
| mass change fraction | 23.0°C,168hr,inSodiumChloride,15% | ISO 1817 | 0.10 % |
| volume change | 23°C,168hr,inHydrochloricAcid,10% | ISO 1817 | 0.40 % |
| 23°C,168hr,inClorox,10% | ASTM D471 | 0.60 % | |
| 23°C,168hr,inCascadeDetergent | ASTM D471 | 0.10 % | |
| Change rate of tensile strength in air | 23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | -20 % |
| 23°C,24hr,inIRM903Oil | ISO 1817 | -4.0 % | |
| mass change fraction | 23°C,168hr,inRelativeHumidity,95% | ASTM D471 | 0.0 % |
| volume change | 23°C,168hr,inSodiumChloride,15% | ASTM D471 | 0.60 % |
| 23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | 0.40 % | |
| mass change fraction | 38°C,168hr,inRelativeHumidity,95% | ASTM D471 | 0.60 % |
| Tensile stress change rate | 23°C,168hr,inSodiumHydroxide,50%，断裂 | ISO 1817 | -18 % |
| Change rate of ultimate elongation in air | 38°C,168hr,inRelativeHumidity,90% | ASTM D471 | -9.0 % |
| volume change | 38°C,168hr,inRelativeHumidity,95% | ASTM D471 | 0.60 % |
| Change rate of tensile strength in air | 23°C,168hr,inEthanol,50% | ASTM D471 | -65 % |
| mass change fraction | 23.0°C,168hr,inHydrochloricAcid,10% | ISO 1817 | 0.40 % |
| volume change | 23°C,168hr,inEthanol,50% | ASTM D471 | 6.8 % |
| Changes in air quality | 100°C,168hr | ASTM D573 | -1.1 % |
| mass change fraction | 23°C,168hr,inEthanol,50% | ASTM D471 | 6.5 % |
| Change rate of tensile strength in air | 23°C,168hr,inSodiumChloride,15% | ISO 1817 | -18 % |
| Tensile stress change rate | 23°C,168hr,inHydrochloricAcid,10%，断裂 | ISO 1817 | -10 % |
| mass change fraction | 23.0°C,168hr,inSodiumHydroxide,50% | ISO 1817 | 0.10 % |
| Change rate of tensile strength in air | 38°C,168hr,inRelativeHumidity,90% | ASTM D471 | -16 % |
| volume change | 38°C,168hr,inRelativeHumidity,95% | ISO 1817 | 0.60 % |
| Shore hardness | ShoreA,23°C,168hr,inDeionizedWater | ISO 1817 | -1.0 |
| Tensile stress change rate | 38°C,168hr,inRelativeHumidity,90%，断裂 | ISO 1817 | -9.0 % |
| volume change | 23°C,168hr,inSodiumChloride,15% | ISO 1817 | 0.60 % |
| Tensile stress change rate | 23°C,168hr,inCascadeDetergent，断裂 | ISO 1817 | -7.0 % |
| Change rate of tensile strength in air | 100°C,168hr | ASTM D573 | 0.0 % |
| 23°C,168hr,inSodiumHydroxide,50% | ISO 1817 | -22 % | |
| Change rate of ultimate elongation in air | 23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | -18 % |
| volume change | 23°C,168hr,inRelativeHumidity,95% | ISO 1817 | 0.0 % |
| Change rate of tensile strength in air | 23°C,168hr,inRelativeHumidity,90% | ASTM D471 | -11 % |
| mass change fraction | 23.0°C,168hr,inClorox,10% | ISO 1817 | 0.60 % |
| Change rate of tensile strength in air | 100°C,168hr | ISO 188 | 0.0 % |
| mass change fraction | 23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | 0.40 % |
| Change rate of tensile strength in air | 23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | -22 % |
| volume change | 23°C,168hr,inCascadeDetergent | ISO 1817 | 0.10 % |
| Change rate of tensile strength in air | 23°C,168hr,inCascadeDetergent | ASTM D471 | -20 % |
| Tensile stress change rate | 23°C,168hr,inClorox,10%，断裂 | ISO 1817 | -4.0 % |
| volume change | 23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | 0.20 % |
| Change rate of tensile strength in air | 23°C,168hr,inEthanol,50% | ISO 1817 | -65 % |
| volume change | 23°C,168hr,inEthanol,50% | ISO 1817 | 6.8 % |
| Hardness change rate in the air | ShoreA,23°C,168hr,inDeionizedWater | ASTM D471 | -1.0 |
| Change rate of tensile strength in air | 38°C,168hr,inRelativeHumidity,90% | ISO 1817 | -16 % |
| 23°C,24hr,inIRM903Oil | ASTM D471 | -4.0 % | |
| Change rate of ultimate elongation in air | 23°C,168hr,inEthanol,50% | ASTM D471 | -66 % |
| 23°C,168hr,inCascadeDetergent | ASTM D471 | -7.0 % | |
| Change rate of tensile strength in air | 23°C,168hr,inClorox,10% | ASTM D471 | -16 % |
| 23°C,168hr,inCascadeDetergent | ISO 1817 | -20 % | |
| 23°C,168hr,inClorox,10% | ISO 1817 | -16 % | |
| Tensile stress change rate | 23°C,168hr,inEthanol,50%，断裂 | ISO 1817 | -66 % |
| Hardness change rate in the air | ShoreA,100°C,672hr | ASTM D573 | -2.0 |
| mass change fraction | 23°C,168hr,inClorox,10% | ASTM D471 | 0.60 % |
| Change rate of ultimate elongation in air | 23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | -10 % |
| mass change fraction | 23.0°C,168hr,inRelativeHumidity,95% | ISO 1817 | 0.0 % |
| 23°C,168hr,inSodiumChloride,15% | ASTM D471 | 0.10 % | |
| 23.0°C,168hr,inCascadeDetergent | ISO 1817 | 0.10 % | |
| elongation at break | 100°C,168hr | ASTM D573 | -11 % |
| Tensile stress change rate | 23°C,168hr,inSodiumChloride,15%，断裂 | ISO 1817 | -6.0 % |
| Changes in air quality | 100°C,168hr | ISO 188 | -1.1 % |
| elastomer | Test Condition | Test Method | CELANESE USA/291-60B150 |
|---|---|---|---|
| elongation | 断裂,23°C，横向 | ASTM D412 | 540 % |
| Tensile stress | 100%应变,23°C，横向流量 | ISO 37 | 2.10 Mpa |
| tensile strength | 断裂,23°C，横向流量 | ASTM D412 | 8.00 Mpa |
| compression set | 23°C,22hr | ISO 815 | 34 % |
| elongation | 断裂,23°C，横向 | ISO 37 | 540 % |
| tear strength | 23°C，Across Flow (横向) | ISO 34-1 | 28 kN/m |
| tensile strength | Break,23°C | ISO 37 | 8.00 Mpa |
| compression set | 70°C,22hr | ASTM D395B | 62 % |
| 70°C,22hr | ISO 815 | 62 % | |
| tear strength | 23°C，横向流量 | ASTM D624 | 28.0 kN/m |
| compression set | 23°C,22hr | ASTM D395B | 34 % |
| Tensile stress | 100%应变,23°C，横向流量 | ASTM D412 | 2.10 Mpa |