POM Delrin®  100P NC010 DUPONT THAILAND

228
  • Unit Price:US$ 3,373 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    60MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High toughness
  • Application Areas:Automotive sector｜Engine parts｜Cam
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Impact strength of cantilever beam gap23°CISO 180/1A14 kJ/m²
Impact strength of cantilever beam gap-40°CISO 180/1A12 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Impact strength of simply supported beam without notch-30°CISO 179/1eU400 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA14 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA15 kJ/m²
flammabilityTest ConditionTest MethodTest Result
Burning rate1.00mmISO 379550 mm/min
UL flame retardant rating0.8mmUL 94HB
UL flame retardant rating1.5mmUL 94HB
UL flame retardant rating0.8mmIEC 60695-11-10,-20HB
UL flame retardant rating1.5mmIEC 60695-11-10,-20HB
FMVSS flammabilityFMVSS302B
Atomizationrefraction，F值ISO 645291 %
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulusISO 527-22950 Mpa
tensile strengthYieldISO 527-271.0 Mpa
Tensile strainYieldISO 527-225 %
Nominal tensile fracture strainISO 527-245 %
Tensile creep modulus1hrISO 899-12700 Mpa
Tensile creep modulus1000hrISO 899-11500 Mpa
Bending modulusISO 1782850 Mpa
bending strength3.5%StrainISO 17877.0 Mpa
Poisson's ratioISO 5270.35
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B155 °C
Linear coefficient of thermal expansionTD：AnnealingTime-OptionalISO 11359-230.0 min/mm
Linear coefficient of thermal expansionTD：AnnealingTemperatureISO 11359-2160 °C
Linear coefficient of thermal expansionTD：-40to23°CISO 11359-21E-04 cm/cm/°C
Linear coefficient of thermal expansionTD：--ISO 11359-21.1E-04 cm/cm/°C
Linear coefficient of thermal expansionMD：-40to23°CISO 11359-21E-04 cm/cm/°C
Linear coefficient of thermal expansionMD：--ISO 11359-21.1E-04 cm/cm/°C
Melting temperatureISO 11357-3178 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A95.0 °C
Vicat softening temperature--ISO 306/A50175 °C
Vicat softening temperature--ISO 306/B50160 °C
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rateEquilibrium,23°C,2.00mm,50%RHISO 620.30 %
Water absorption rateSaturation,23°C,2.00mmISO 621.4 %
Shrinkage rateMDISO 294-42.2 %
Shrinkage rateTDISO 294-41.9 %
Melt Volume Flow Rate (MVR)190°C/2.16kgISO 11332.20 cm3/10min
melt mass-flow rateISO 11332.6 g/10min
densityISO 11831.42 g/cm³
MediumDensity1.19 g/cm³
SpecificHeatCapacity of Melt3000 J/kg/°C
ThermalConductivityofMelt0.22 W/m/K
Electrical performanceTest ConditionTest MethodTest Result
Dielectric strengthIEC 60243-141 KV/mm
Volume resistivityIEC 600931E+14 ohms·cm
Surface resistivityIEC 600932E+13 ohms
Relative permittivity100HzIEC 602503.90
Relative permittivity1MHzIEC 602503.90
Dissipation factor100HzIEC 602503.5E-03
Dissipation factor1MHzIEC 602505.5E-03
Compared to the anti leakage trace indexIEC 60112PLC 0
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-SaleISO 2039-2119
Rockwell hardnessM-SaleISO 2039-288
Supplementary InformationTest ConditionTest MethodTest Result
EmissionVDA275<8.00 mg/kg
EmissionofOrganicCompoundsVDA2774.70 µgC/g
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.