Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM 100P NC010 DUPONT THAILAND
Delrin®
Automotive sector、Engine parts、Cam
High toughness
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT THAILAND/100P NC010 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 15 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 14 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 14 kJ/m² |
| -40°C | ISO 180/1A | 12 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 400 kJ/m² |
| hardness | Test Condition | Test Method | DUPONT THAILAND/100P NC010 |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 119 |
| M计秤 | ISO 2039-2 | 88 |
| Supplementary Information | Test Condition | Test Method | DUPONT THAILAND/100P NC010 |
|---|---|---|---|
| Emission | VDA275 | <8.00 mg/kg | |
| Emissions of Organic Compounds | VDA277 | 4.70 µgC/g |
| Electrical performance | Test Condition | Test Method | DUPONT THAILAND/100P NC010 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| dielectric strength | IEC 60243-1 | 41 KV/mm | |
| Volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 3.90 |
| Dissipation Factor | 100Hz | IEC 60250 | 3.5E-03 |
| relative permittivity | 1MHz | IEC 60250 | 3.90 |
| Surface Resistivity | IEC 60093 | 2E+13 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 5.5E-03 |
| Mechanical properties | Test Condition | Test Method | DUPONT THAILAND/100P NC010 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2950 Mpa | |
| Tensile creep modulus | 1hr | ISO 899-1 | 2700 Mpa |
| Nominal tensile fracture strain | ISO 527-2 | 45 % | |
| Flexural modulus | ISO 178 | 2850 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 25 % |
| Tensile creep modulus | 1000hr | ISO 899-1 | 1500 Mpa |
| tensile strength | 屈服 | ISO 527-2 | 71.0 Mpa |
| bending strength | 3.5%应变 | ISO 178 | 77.0 Mpa |
| Poisson's ratio | ISO 527 | 0.35 |
| flammability | Test Condition | Test Method | DUPONT THAILAND/100P NC010 |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | IEC 60695-11-10,-20 | HB |
| atomization | refraction，F值 | ISO 6452 | 91 % |
| UL flame retardant rating | 1.5mm | IEC 60695-11-10,-20 | HB |
| FMVSS flammability | FMVSS302 | B | |
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| 1.5mm | UL 94 | HB | |
| burning rate | 1.00mm | ISO 3795 | 50 mm/min |
| physical property | Test Condition | Test Method | DUPONT THAILAND/100P NC010 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 2.20 cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 1.9 % |
| MD | ISO 294-4 | 2.2 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 1.4 % |
| melt mass-flow rate | ISO 1133 | 2.6 g/10min | |
| MediumDensity | 1.19 g/cm³ | ||
| density | ISO 1183 | 1.42 g/cm³ | |
| SpecificHeatCapacity of Melt | 3000 J/kg/°C | ||
| ThermalConductivityofMelt | 0.22 W/m/K | ||
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.30 % |
| Thermal performance | Test Condition | Test Method | DUPONT THAILAND/100P NC010 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 178 °C | |
| Linear coefficient of thermal expansion | TD：-- | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| MD：-40to23°C | ISO 11359-2 | 1E-04 cm/cm/°C | |
| TD：-40to23°C | ISO 11359-2 | 1E-04 cm/cm/°C | |
| MD：-- | ISO 11359-2 | 1.1E-04 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 155 °C |
| Linear coefficient of thermal expansion | TD：AnnealingTemperature | ISO 11359-2 | 160 °C |
| vicat | -- | ISO 306/A50 | 175 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 95.0 °C |
| vicat | -- | ISO 306/B50 | 160 °C |
| Linear coefficient of thermal expansion | TD：AnnealingTime-Optional | ISO 11359-2 | 30.0 min/mm |