SMMA HX208 LG CHEM KOREA
232
- Unit Price:US$ 2,288 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 8.0 g/10 min | |
| Shrinkage rate | ASTM D955 | 0.20 - 0.60 % | |
| Water absorption rate | ASTM D570 | 0.12 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 75 |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | ISO 489 | 1.550 | |
| transmissivity | ISO 13468-1 | 91.0 % | |
| ISO 13468-1 | 82.0 % | ||
| Haze ratio | ISO 14782 | < 0.50 % | |
| ISO 14782 | 6.5 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flammability level | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 3100 Mpa | |
| tensile strength | ISO 527-2/5 | 62.0 Mpa | |
| Tensile strain | ISO 527-2/5 | 3.0 % | |
| Flexural modulus | ISO 178 | 3100 Mpa | |
| bending strength | ISO 178 | 100 Mpa |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | < 80 °C | ||
| Drying time - hot air dryer | 3.0 to 4.0 hr | ||
| Temperature at the rear of the barrel | 210 to 240 °C | ||
| Temperature in the middle of the barrel | 210 to 240 °C | ||
| Temperature at the front of the material cylinder | 210 to 240 °C | ||
| Processing (melt) temperature | 210 to 240 °C | ||
| Temperature | 50 to 70 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/A | 90.0 °C | |
| vicat | ISO 306/B50 | 95.0 °C | |
| Linear coefficient of thermal expansion | ASTM D696 | 6.0E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.