PC/PBT

PC/PBT XENOY™ X5630P SABIC INNOVATIVE US

264

Unit Price:US$ 3,681 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
53MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜High impact resistance｜Dimensional stability
Application Areas:Automotive Applications
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	6.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	8.0 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	80 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	100 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1	4150 Mpa
tensile strength	Yield	ISO 527-2/5	56.0 Mpa
tensile strength	tensile strength	Break	ISO 527-2/5	50.0 Mpa
Tensile strain	Yield	ISO 527-2/5	3.2 %
Tensile strain	Tensile strain	Break	ISO 527-2/5	8.0 %
Bending modulus		ISO 178	4050 Mpa
bending strength		ISO 178	90.0 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			110 to 120 °C
drying time			4.0 to 6.0 hr
Suggested maximum moisture content			0.020 %
Hopper temperature			60 to 80 °C
Temperature at the rear of the barrel			240 to 270 °C
Temperature in the middle of the barrel			250 to 275 °C
Temperature at the front of the material cylinder			260 to 280 °C
Spray nozzle temperature			260 to 275 °C
Processing (melt) temperature			265 to 275 °C
Mold temperature			60 to 100 °C

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span	ISO 75-2/Af	110 °C
Vicat softening temperature	--	ISO 306/B50	137 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	140 °C
Linear coefficient of thermal expansion	Flow : -30 to 80°C	ISO 11359-2	5.2E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -30 to 80°C	ISO 11359-2	7.2E-5 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Melt Volume Flow Rate (MVR)	265°C/5.0 kg	ISO 1133	15.0 cm3/10min
Water absorption rate	Saturation, 23°C	ISO 62	0.42 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.14 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/PBT XENOY™ X5630P SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet