Certificates
PC/PBT X5630P SABIC INNOVATIVE US
XENOY™
Automotive Applications
High mobility、High impact resistance、Dimensional stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/X5630P |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 80 kJ/m² |
| 23°C | ISO 180/1U | 100 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 6.0 kJ/m² |
| 23°C | ISO 180/1A | 8.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/X5630P |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 4150 Mpa | |
| tensile strength | 屈服 | ISO 527-2/5 | 56.0 Mpa |
| 断裂 | ISO 527-2/5 | 50.0 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/5 | 3.2 % |
| bending strength | ISO 178 | 90.0 Mpa | |
| Flexural modulus | ISO 178 | 4050 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 8.0 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/X5630P |
|---|---|---|---|
| Melt volume flow rate | 265°C/5.0 kg | ISO 1133 | 15.0 cm3/10min |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.14 % |
| 饱和, 23°C | ISO 62 | 0.42 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/X5630P |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 140 °C |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距，HDT | ISO 75-2/Af | 110 °C |
| vicat | -- | ISO 306/B50 | 137 °C |
| Linear coefficient of thermal expansion | 横向 : -30 到 80°C | ISO 11359-2 | 7.2E-5 cm/cm/°C |
| 流动 : -30 到 80°C | ISO 11359-2 | 5.2E-5 cm/cm/°C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/X5630P |
|---|---|---|---|
| drying time | 4.0 to 6.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 250 to 275 °C | ||
| Temperature at the rear of the barrel | 240 to 270 °C | ||
| Processing (melt) temperature | 265 to 275 °C | ||
| Hopper temperature | 60 to 80 °C | ||
| drying temperature | 110 to 120 °C | ||
| Temperature at the front of the material cylinder | 260 to 280 °C | ||
| Temperature | 60 to 100 °C | ||
| Spray nozzle temperature | 260 to 275 °C |