ABS

ABS XR401HF NP LG CHEM KOREA

251

Unit Price:US$ 1,046 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Low gloss｜UV resistance
Application Areas:Shell｜Automotive Applications｜Automotive interior parts｜Automotive External Parts
Color:--
Grade:Heat resistant grade

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	75.0 Mpa
bending strength	bending strength	3.20mm	ASTM D790	78.5 Mpa
Bending modulus		ISO 178	2350 Mpa
Bending modulus	Bending modulus	3.20mm	ASTM D790	2550 Mpa
elongation	Break,3.20mm	ASTM D638	20 %
tensile strength	Yield	ISO 527-2/50	49.0 Mpa
tensile strength	tensile strength	Yield,3.20mm	ASTM D638	49.0 Mpa
Tensile modulus		ISO 527-2/1	2300 Mpa

thermal performance	Test Condition	Test Method	Test Result
RTI Str		UL 746	60.0 °C
RTI Imp		UL 746	60.0 °C
RTI Elec		UL 746	60.0 °C
Linear coefficient of thermal expansion	TD：23to60°C	ISO 11359-2	8.0E-5to9.0E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to60°C	ISO 11359-2	8.0E-5to9.0E-5 cm/cm/°C
Vicat softening temperature		ISO 306/B50	106 °C
Vicat softening temperature	Vicat softening temperature		ASTM D15256	106 °C
Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/Ae	88.0 °C
	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	97.0 °C
		Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/Be	95.0 °C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	106 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	220°C/10.0kg	ASTM D1238	9.0 g/10min
Shrinkage rate	MD：3.20mm	ISO 294-4	0.40-0.70 %
Shrinkage rate	Shrinkage rate	MD：3.20mm	ASTM D955	0.40-0.70 %
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	9.00 cm3/10min

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity	23°C	ASTM D257	1.5E+03 ohms·cm
Dielectric strength	23°C,1.00mm	ASTM D149	33 KV/mm
Arc resistance		ASTM D495	PLC6

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	110
Rockwell hardness	Rockwell hardness		ISO 2039-2	112

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.