ABS XR401HF NP LG CHEM KOREA
--
Shell、Automotive Applications、Automotive interior parts、Automotive External Parts
Low gloss、UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodLG CHEM KOREA/XR401HF NP
Rockwell hardnessISO2039-2112
R级ASTMD785110
Mechanical propertiesTest ConditionTest MethodLG CHEM KOREA/XR401HF NP
Tensile stress屈服ISO527-2/5049.0 Mpa
Tensile modulusISO527-2/12300 Mpa
Flexural Strength33.20mmASTMD79078.5 Mpa
elongation断裂,3.20mmASTMD63820 %
Bending stressISO17875.0 Mpa
Flexural modulusISO1782350 Mpa
3.20mmASTMD7902550 Mpa
tensile strength屈服,3.20mmASTMD63849.0 Mpa
Electrical performanceTest ConditionTest MethodLG CHEM KOREA/XR401HF NP
arc resistanceASTMD495PLC6
dielectric strength23°C,1.00mmASTMD14933 KV/mm
Volume resistivity23°CASTMD2571.5E+03 ohms·cm
flammabilityTest ConditionTest MethodLG CHEM KOREA/XR401HF NP
UL flame retardant ratingUL94HB
physical property Test ConditionTest MethodLG CHEM KOREA/XR401HF NP
Shrinkage rateMD：3.20mmASTMD9550.40to0.70 %
Melt volume flow rate220°C/10.0kgISO11339.00 cm3/10min
Shrinkage rateMD：3.20mmISO294-40.40to0.70 %
melt mass-flow rate220°C/10.0kgASTMD12389.0 g/10min
Thermal performanceTest ConditionTest MethodLG CHEM KOREA/XR401HF NP
Hot deformation temperature 51.8MPa,Unannealed,4.00mmISO75-2/Ae88.0 °C
vicatISO306/B50106 °C
TD：23to60°CISO11359-28.0E-5to9.0E-5 cm/cm/°C
RTI StrUL74660.0 °C
RTI ElecUL74660.0 °C
1.8MPa,未退火,6.40mmASTMD64897.0 °C
Hot deformation temperature 50.45MPa,Unannealed,4.00mmISO75-2/Be95.0 °C
MD：23到60°CISO11359-28.0E-5to9.0E-5 cm/cm/°C
vicatASTMD15256106 °C
RTI ImpUL74660.0 °C
0.45MPa,未退火,6.40mmASTMD648106 °C