PA66 Ultramid® A3EG10 BASF GERMANY
264
- Unit Price:US$ 3,406 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:71MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Oil resistant｜High rigidity
- Application Areas:Industrial components｜Electronic insulation
- Color:--
- Grade:Enhanced level
Material Certification
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | 222.76to370.34 MPa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | 260 ℃（℉） | ||
| Heat Deflection Temperature | 0.45Mpa | ISO 75-2 | 250 ℃ |
| UL flame retardant rating | UL94 | HB | |
| Heat Deflection Temperature | 1.8Mpa | ISO 75-2 | 250 ℃ |
| Continuous use temperature | °C | 110to220 | |
| 8.0Mpa, Not annealed | °C | 65to220 | |
| 1.8MPa, Not annealed | °C | 230to250 | |
| horizontal | mm/mm/°C | 68.6E-5-127.0E-5 | |
| flow | mm/mm/°C | 142.2E-5-203.2E-5 | |
| melting temperature | °C | 260 |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| purpose | 高机械强度 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 11.143to19.964 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | ASTM D257/IEC 60093 | 1E 13 Ω.cm | |
| dielectric constant | 1MHz | IEC 60250 | 3.8 |
| Dielectric loss | 1MHz | IEC 60250 | 0.015 |
| volume resistivity | IEC 60093 | Ω.M | |
| Surface Resistivity | IEC 60093 | Ω | |
| dielectric strength | 23℃ | V/mil | 840 |
| volume resistivity | 23℃ | ohms·cm | 1.0E+12-1.0E+14 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1560 | |
| Water absorption rate | ASTM D570/ISO 62 | 3.7-4.3 % | |
| Saturation, 23 ℃ | % | 3.5to5.0 | |
| Balance, 23 ℃, 50% RH | % | 1.2to1.5 | |
| shrinkage rate | 23℃ | % | 0.10-0.31 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 13 kg·cm/cm(J/M)ft·lb/in | |
| Tensile modulus | ASTM D638/ISO 527 | 16800 kg/cm²(MPa)[Lb/in²] | |
| flexural modulus | ASTM D790/ISO 178 | 15000 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 360 kg·cm/cm(J/M)ft·lb/in | |
| Tensile stress | 屈服 | ISO 527-2 | 230 MPa |
| Charpy Notched Impact Strength | ISO 179/1eA | 18 KJ/m | |
| tensile strength | 断裂,23℃ | 144.83to292.41 MPa | |
| Tensile modulus | 23℃ | 8206.9to28000.0 MPa | |
| Tensile strain | 断裂,23℃ | % | 1.9to3.1 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.