PA66 A3EG10 BASF GERMANY
Ultramid®
Industrial components,Electronic insulation
Oil resistant,High rigidity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | BASF GERMANY/A3EG10 |
---|---|---|---|
Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 11.143to19.964 |
hardness | Test Condition | Test Method | BASF GERMANY/A3EG10 |
---|---|---|---|
ball-indentation hardness | 222.76to370.34 MPa |
Electrical performance | Test Condition | Test Method | BASF GERMANY/A3EG10 |
---|---|---|---|
Dielectric loss | 1MHz | IEC 60250 | 0.015 |
dielectric strength | 23℃ | V/mil | 840 |
Volume resistivity | IEC 60093 | Ω.M | |
dielectric constant | 1MHz | IEC 60250 | 3.8 |
Volume resistivity | ASTM D257/IEC 60093 | 1E 13 Ω.cm | |
23℃ | ohms·cm | 1.0E+12-1.0E+14 | |
Surface Resistivity | IEC 60093 | Ω |
Mechanical properties | Test Condition | Test Method | BASF GERMANY/A3EG10 |
---|---|---|---|
Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 13 kg·cm/cm(J/M)ft·lb/in | |
Tensile strain | 断裂,23℃ | % | 1.9to3.1 |
Tensile stress | 屈服 | ISO 527-2 | 230 MPa |
Charpy Notched Impact Strength | ISO 179/1eA | 18 KJ/m | |
Tensile modulus | ASTM D638/ISO 527 | 16800 kg/cm²(MPa)[Lb/in²] | |
tensile strength | 断裂,23℃ | 144.83to292.41 MPa | |
Flexural modulus | ASTM D790/ISO 178 | 15000 kg·cm/cm(J/M)ft·lb/in | |
bending strength | ASTM D790/ISO 178 | 360 kg·cm/cm(J/M)ft·lb/in | |
Tensile modulus | 23℃ | 8206.9to28000.0 MPa |
other | Test Condition | Test Method | BASF GERMANY/A3EG10 |
---|---|---|---|
purpose | 高机械强度 |
Physical properties | Test Condition | Test Method | BASF GERMANY/A3EG10 |
---|---|---|---|
density | ASTM D792/ISO 1183 | 1560 | |
Water absorption rate | ASTM D570/ISO 62 | 3.7-4.3 % |
physical property | Test Condition | Test Method | BASF GERMANY/A3EG10 |
---|---|---|---|
Balance, 23 ℃, 50% RH | % | 1.2to1.5 | |
Saturation, 23 ℃ | % | 3.5to5.0 | |
Shrinkage rate | 23℃ | % | 0.10-0.31 |
Thermal performance | Test Condition | Test Method | BASF GERMANY/A3EG10 |
---|---|---|---|
8.0Mpa, Not annealed | °C | 65to220 | |
Continuous use temperature | °C | 110to220 | |
Heat distortion temperature | 0.45Mpa,HDT | ISO 75-2 | 250 ℃ |
flow | mm/mm/°C | 142.2E-5-203.2E-5 | |
Heat distortion temperature | 1.8Mpa,HDT | ISO 75-2 | 250 ℃ |
1.8MPa, Not annealed | °C | 230to250 | |
melting temperature | 260 ℃(℉) | ||
UL flame retardant rating | UL94 | HB | |
horizontal | mm/mm/°C | 68.6E-5-127.0E-5 | |
melting temperature | °C | 260 |