PA66

PA66 66 MV HI LYONDELLBASELL GERMANY

321

Unit Price:US$ 6,289 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Toughened grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C		无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C		无断裂

flammability	Test Condition	Test Method	Test Result
Burning wire flammability index	3.0 mm		600 °C
Burning wire flammability index	Burning wire flammability index	1.5 mm		600 °C
Flammability level	3.0 mm		HB
	Flammability level	1.5 mm		HB
	Flammability level	Flammability level	0.75 mm		HB
Burning rate	2.00 mm	FMVSS 302	30 mm/min
Burning rate	Burning rate	2.00 mm	ISO 3795	30 mm/min

mechanical properties	Test Method	Test Result
Tensile strain (yield)	ISO 527-2/1A/50	5 %
Tensile stress (yield)	ISO 527-2/1A/50	65 Mpa
Tensile modulus	ISO 527-1/1A/1	2500 Mpa

injection	Test Condition	Test Method	Test Result
Suggested maximum moisture content			0.040 to 0.10
Processing (melt) temperature			270 to 290
Mold temperature			60 to 100
drying time			3.0 to 4.0
drying temperature			80

thermal performance	Test Condition	Test Method	Test Result
Ball Pressure Test	(60°C)	IEC 60695-10-2	通过
Vicat softening temperature	--	ISO 306/A50	230 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	215 °C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/Af	60 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/Bf	170 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	2.1 %

Electrical performance	Test Method	Test Result
Compared to the anti leakage trace index	IEC 60112	PLC 0
Volume resistivity	IEC 62631-3-1	> 1.0E+13 ohms·m
Surface resistivity	IEC 60093	> 1.0E+15 ohms

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test		ISO 2039-1	110 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.