Product Name / Manufacturer / Model

Grade

Reference Price

PA66 LYONDELLBASELL GERMANY 66 MV HI

Toughened grade

US$ 4,410 / MT

FOB Shenzhen Port

thermal performance	Test Condition	Test Method	LYONDELLBASELL GERMANY/66 MV HI
Vicat softening temperature	--	ISO 306/B50	215 °C
Vicat softening temperature		--	ISO 306/A50	230 °C
Ball Pressure Test	(60°C)	IEC 60695-10-2	通过
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/Bf	170 °C
Hot deformation temperature		1.8 MPa, Unannealed	ISO 75-2/Af	60 °C
flammability	Test Condition	Test Method	LYONDELLBASELL GERMANY/66 MV HI
Burning rate	2.00 mm	ISO 3795	30 mm/min
Burning rate		2.00 mm	FMVSS 302	30 mm/min
Flammability level	0.75 mm		HB
		1.5 mm		HB
		3.0 mm		HB
Burning wire flammability index	3.0 mm		600 °C
Burning wire flammability index		1.5 mm		600 °C
mechanical properties	Test Condition	Test Method	LYONDELLBASELL GERMANY/66 MV HI
Tensile modulus		ISO 527-1/1A/1	2500 Mpa
Tensile strain (yield)		ISO 527-2/1A/50	5 %
Tensile stress (yield)		ISO 527-2/1A/50	65 Mpa
hardness	Test Condition	Test Method	LYONDELLBASELL GERMANY/66 MV HI
Ball Pressure Test		ISO 2039-1	110 Mpa
Physical properties	Test Condition	Test Method	LYONDELLBASELL GERMANY/66 MV HI
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	2.1 %
injection	Test Condition	Test Method	LYONDELLBASELL GERMANY/66 MV HI
Mold temperature			60 to 100
drying temperature			80
Processing (melt) temperature			270 to 290
drying time			3.0 to 4.0
Suggested maximum moisture content			0.040 to 0.10
Electrical performance	Test Condition	Test Method	LYONDELLBASELL GERMANY/66 MV HI
Compared to the anti leakage trace index		IEC 60112	PLC 0
Volume resistivity		IEC 62631-3-1	> 1.0E+13 ohms·m
Surface resistivity		IEC 60093	> 1.0E+15 ohms
impact performance	Test Condition	Test Method	LYONDELLBASELL GERMANY/66 MV HI
Impact strength of simply supported beam without notch	23°C		无断裂
Impact strength of simply supported beam without notch		-30°C		无断裂