Material Description

Material Properties:Glass fiber reinforced｜high strength｜High rigidity｜High temperature resistance
Application Areas:Electrical field｜Electronic field｜Automotive sector｜Bottle cap｜sporting goods｜Electrical appliances
Color:--
Grade:Injection grade

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			PA66.13％玻纤增强.热稳定.注塑树脂

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	40 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	40 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	35 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	40 kJ/m²

flammability	Test Condition	Test Method	Test Result
Burning rate	1.00mm	ISO 3795	27 mm/min
UL flame retardant rating	0.71mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
		UL flame retardant rating	0.71mm	IEC 60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
Extreme Oxygen Index		ISO 4589-2	24 %
FMVSS flammability		FMVSS302	B

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ASTM D790/ISO 178	190 kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	3 %
Charpy Notched Impact Strength		ASTM D256/ISO 179	4.5 (-40℃) kg·cm/cm(J/M)ft·lb/in
	Charpy Notched Impact Strength		ASTM D256/ISO 179	30 kg·cm/cm(J/M)ft·lb/in
		Charpy Notched Impact Strength		ASTM D256/ISO 179	32 kg·cm/cm(J/M)ft·lb/in
		Charpy Notched Impact Strength	Charpy Notched Impact Strength		ASTM D256/ISO 179	5 kg·cm/cm(J/M)ft·lb/in
Tensile modulus		ISO 527-2	5500 Mpa
Bending modulus		ASTM D790/ISO 178	4900 kg·cm/cm(J/M)ft·lb/in
tensile strength		ASTM D638/ISO 527	120 kg/cm²(MPa)[Lb/in²]
Tensile modulus		ASTM D638/ISO 527	5500 kg/cm²(MPa)[Lb/in²]
Wear resistance		ISO 4649	10.0 mm³
tensile strength	Break	ISO 527-2	120 Mpa
Tensile strain	Break	ISO 527-2	3.0 %
Tensile creep modulus	1hr	ISO 899-1	-- Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	-- Mpa
Bending modulus		ISO 178	4800 Mpa
bending strength		ISO 178	190 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	HDT	ASTM D648/ISO 75	238 ℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	258 ℃（℉）
Combustibility (rate)		UL 94	HB
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	0.77 mm/mm.℃
Melting temperature			262 ℃（℉）
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	258 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	238 °C
Glass transition temperature		ISO 11357-2	80.0 °C
Vicat softening temperature		ISO 306/B50	205 °C
Melting temperature		ISO 11357-3	262 °C
Linear coefficient of thermal expansion	MD：--	ISO 11359-2	4E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	4.2E-05 cm/cm/°C
		Linear coefficient of thermal expansion	MD：55to160°C	ISO 11359-2	2.6E-05 cm/cm/°C
			Linear coefficient of thermal expansion	TD：--	ISO 11359-2	9.3E-05 cm/cm/°C
				Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	7.7E-05 cm/cm/°C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：55to160°C	ISO 11359-2	1.5E-04 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	2.2 %
	Water absorption rate	Saturation,23°C,2.00mm	ISO 62	7.6 %
		Water absorption rate	23°C,24hr	ISO 62	1.7 %
		Water absorption rate	Water absorption rate		ASTM D570/ISO 62	2.2 %
Shrinkage rate		ASTM D955	0.7-1.2 %
density		ASTM D792/ISO 1183	1.23
Shrinkage rate	MD	ISO 294-4	0.70 %
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	1.2 %
Top out temperature			210 °C

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	-- ohms
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Dielectric strength		IEC 60243-1	25 KV/mm
Relative permittivity	100Hz	IEC 60250	3.90
Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.20
Dissipation factor	100Hz	IEC 60250	0.013
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.015

Supplementary Information	Test Condition	Test Method	Test Result
EmissionofOrganicCompounds		VDA277	6.00 µgC/g

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 Zytel® 70G13L NC010 DUPONT USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet