Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 70G13L NC010 DUPONT USA
Zytel® 
Electrical field,Electronic field,Automotive sector,Bottle cap,sporting goods,Electrical appliances
Glass fiber reinforced,high strength,High rigidity,High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodDUPONT USA/70G13L NC010
Suspended wall beam without notch impact strength-30°CISO 180/1U35 kJ/m²
23°CISO 180/1U40 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU40 kJ/m²
-30°CISO 179/1eU40 kJ/m²
Supplementary InformationTest ConditionTest MethodDUPONT USA/70G13L NC010
Emissions of Organic CompoundsVDA2776.00 µgC/g
thermal performanceTest ConditionTest MethodDUPONT USA/70G13L NC010
Heat Deflection Temperature0.45MPa,未退火，HDTISO 75-2/B258 °C
Linear coefficient of thermal expansionMD：--ISO 11359-24E-05 cm/cm/°C
MD：55to160°CISO 11359-22.6E-05 cm/cm/°C
ASTM D696/ISO 113590.77 mm/mm.℃
Glass Transition TemperatureISO 11357-280.0 °C
melting temperatureISO 11357-3262 °C
262 ℃（℉）
Heat Deflection Temperature1.8MPa,未退火，HDTISO 75-2/A238 °C
Linear coefficient of thermal expansionTD：-40to23°CISO 11359-27.7E-05 cm/cm/°C
Heat Deflection TemperatureHDTASTM D648/ISO 75238 ℃（℉）
Combustibility (rate)UL 94HB
vicatISO 306/B50205 °C
Linear coefficient of thermal expansionMD：-40to23°CISO 11359-24.2E-05 cm/cm/°C
TD：--ISO 11359-29.3E-05 cm/cm/°C
TD：55to160°CISO 11359-21.5E-04 cm/cm/°C
Mechanical propertiesTest ConditionTest MethodDUPONT USA/70G13L NC010
Tensile modulusISO 527-25500 Mpa
tensile strength断裂ISO 527-2120 Mpa
Tensile creep modulus1000hrISO 899-1-- Mpa
wear resistanceISO 464910.0 mm³
flexural modulusASTM D790/ISO 1784900 kg·cm/cm(J/M)ft·lb/in
bending strengthASTM D790/ISO 178190 kg·cm/cm(J/M)ft·lb/in
Elongation at breakASTM D638/ISO 5273 %
Tensile creep modulus1hrISO 899-1-- Mpa
bending strengthISO 178190 Mpa
Tensile strain断裂ISO 527-23.0 %
tensile strengthASTM D638/ISO 527120 kg/cm²(MPa)[Lb/in²]
flexural modulusISO 1784800 Mpa
Tensile modulusASTM D638/ISO 5275500 kg/cm²(MPa)[Lb/in²]
Charpy Notched Impact StrengthASTM D256/ISO 1794.5 (-40℃) kg·cm/cm(J/M)ft·lb/in
Electrical performanceTest ConditionTest MethodDUPONT USA/70G13L NC010
dielectric strengthIEC 60243-125 KV/mm
relative permittivity100HzIEC 602503.90
Dissipation Factor100HzIEC 602500.013
volume resistivityIEC 60093>1.0E+15 ohms·cm
relative permittivity1MHzIEC 602503.20
Surface ResistivityIEC 60093-- ohms
Dissipation Factor1MHzIEC 602500.015
otherTest ConditionTest MethodDUPONT USA/70G13L NC010
characteristicPA66.13％玻纤增强.热稳定.注塑树脂
Physical propertiesTest ConditionTest MethodDUPONT USA/70G13L NC010
Water absorption rate平衡,23°C,2.00mm,50%RHISO 622.2 %
shrinkage rateASTM D9550.7-1.2 %
densityASTM D792/ISO 11831.23
shrinkage rateTDISO 294-41.2 %
Ejection Temperature210 °C
Water absorption rate饱和,23°C,2.00mmISO 627.6 %
shrinkage rateMDISO 294-40.70 %
Water absorption rate23°C,24hrISO 621.7 %
ASTM D570/ISO 622.2 %
flammabilityTest ConditionTest MethodDUPONT USA/70G13L NC010
UL flame retardant rating1.5mmIEC 60695-11-10,-20HB
FMVSS flammabilityFMVSS302B
UL flame retardant rating0.71mmIEC 60695-11-10,-20HB
1.5mmUL 94HB
Limiting Oxygen IndexISO 4589-224 %
burning rate1.00mmISO 379527 mm/min
UL flame retardant rating0.71mmUL 94HB