PA66 Leona™ 1300S ASAHI JAPAN

803

Unit Price:US$ 3,210 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
279.11MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
PA66 Vydyne® 21SPC ASCEND USA

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜High rigidity｜Good flexibility
Application Areas:Laptop case｜Automotive sector｜parts｜Consumer goods sector
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			标准.流动
Other performance	Test Condition	Test Method	Test Result	Test Unit
Extreme Oxygen Index	干	ASTM D-2863	26	%
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL -94	V-2	0.40mm
	UL flame retardant rating		UL -94	V-2	0.71mm
		UL flame retardant rating		UL -94	V-2	1.50mm
		UL flame retardant rating	UL flame retardant rating		UL -94	V-2	3.00mm
Extreme Oxygen Index		ASTM2863	26	%
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	湿		2.5	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	干(湿)	ASTM D-785	80(55)	M Scale
Impact strength of cantilever beam gap	干(湿)	ASTM D-256	39(147)	J/m
tensile strength	干(湿)	ASTM D-638	79(57)	Mpa
Elongation at Break	干(湿)	ASTM D-638	50(250)	%
Rockwell hardness	干(湿)	ASTM D-785	120(108)	R scale
bending strength	干(湿)	ASTM D-790	118(54)	Mpa
flexural coefficient	干(湿)	ASTM D-790	2.8(1.2)	GPa
Wear factor	湿	ASTM D-1044	7
Elongation at Break	23°C	ASTM D638	50	%
bending strength	23°C	ASTM D790	118	Mpa
Bending modulus	23°C	ASTM D790	2800	Mpa
Impact strength of cantilever beam gap	23°C	ASTM D256	39	J/m
tensile strength	23°C	ASTM D638	79	Mpa
Charpy Notched Impact Strength		ASTM D256/ISO 179	39	kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	50	%
tensile strength		ASTM D638/ISO 527	-	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	2790	kg·cm/cm(J/M)ft·lb/in
bending strength		ASTM D790/ISO 178	118	kg·cm/cm(J/M)ft·lb/in
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.46MPa,干	ASTM D-648	230	°C
Hot deformation temperature	Hot deformation temperature	1.82MPa,干	ASTM D-648	70	°C
UL flame retardant rating	干	UL 94	V-2
Linear coefficient of thermal expansion	干	ASTM D-696	8
thermal conductivity	干		0.2	W/(m.K)
specific heat	干		1670	J/(kg.k)
Hot deformation temperature	0.45MPaUnannealed	ASTM D648	230	°C
Hot deformation temperature	Hot deformation temperature	1.80MPaUnannealed	ASTM D648	70	°C
Linear coefficient of thermal expansion	导热系数	JISR2618	0.2	W/m/K
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	比热		1670	J/kg/°C
Combustibility (rate)		UL 94	v-2
Hot deformation temperature	HDT	ASTM D648/ISO 75	230	℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	8	mm/mm.℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	干	旭化成方法	1.3-2.0	%
	Shrinkage rate	MD2.0mm	ASTM D995	1.3	%
	Shrinkage rate	Shrinkage rate	TD2.0mm	ASTM D995	2.0	%
Water absorption rate	(23°C,24hr)	ASTM D570	2.5	%
density		ASTM D792/ISO 1183	1.14
Water absorption rate		ASTM D570/ISO 62	2.5	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength		ASTM D149	20	KV/mm
Dissipation factor	相对漏电起痕指数	ASTM D3638	600	V
Volume resistivity		ASTM D257/IEC 60093	10-10	Ω.cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness		ASTM D785	80	M（Scale）
Rockwell hardness	Rockwell hardness		ASTM D785	120	R

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.