PA66 1300S PA66 vs. - Plastic Material Properties Comparison Chart at Plas.com

mechanical properties	Test Condition	Test Method	ASAHI JAPAN/1300S
tensile strength	23°C	ASTM D638	79 Mpa
Bending modulus	23°C	ASTM D790	2800 Mpa
Rockwell hardness	干(湿)	ASTM D-785	120(108) M Scale
Wear factor	湿	ASTM D-1044	7
Charpy Notched Impact Strength		ASTM D256/ISO 179	39 kg·cm/cm(J/M)ft·lb/in
bending strength	干(湿)	ASTM D-790	118(54) Mpa
Impact strength of cantilever beam gap	23°C	ASTM D256	39 J/m
bending strength		ASTM D790/ISO 178	118 kg·cm/cm(J/M)ft·lb/in
tensile strength	干(湿)	ASTM D-638	79(57) Mpa
flexural coefficient	干(湿)	ASTM D-790	2.8(1.2) GPa
Elongation at Break		ASTM D638/ISO 527	50 %
Elongation at Break		23°C	ASTM D638	50 %
Impact strength of cantilever beam gap	干(湿)	ASTM D-256	39(147) J/m
bending strength	23°C	ASTM D790	118 Mpa
Elongation at Break	干(湿)	ASTM D-638	50(250) %
Bending modulus		ASTM D790/ISO 178	2790 kg·cm/cm(J/M)ft·lb/in
tensile strength		ASTM D638/ISO 527	- kg/cm²(MPa)[Lb/in²]
Physical properties	Test Condition	Test Method	ASAHI JAPAN/1300S
Water absorption rate		ASTM D570/ISO 62	2.5 %
Shrinkage rate	MD2.0mm	ASTM D995	1.3 %
Shrinkage rate		干	旭化成方法	1.3-2.0 %
Water absorption rate	(23°C,24hr)	ASTM D570	2.5 %
Shrinkage rate	TD2.0mm	ASTM D995	2.0 %
density		ASTM D792/ISO 1183	1.14
thermal performance	Test Condition	Test Method	ASAHI JAPAN/1300S
Hot deformation temperature	HDT	ASTM D648/ISO 75	230 ℃（℉）
		0.46MPa,干	ASTM D-648	230 °C
		1.82MPa,干	ASTM D-648	70 °C
		0.45MPaUnannealed	ASTM D648	230 °C
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	8 mm/mm.℃
Linear coefficient of thermal expansion		比热		1670 J/kg/°C
thermal conductivity	干		0.2 W/(m.K)
Linear coefficient of thermal expansion	干	ASTM D-696	8
Hot deformation temperature	1.80MPaUnannealed	ASTM D648	70 °C
UL flame retardant rating	干	UL 94	V-2
Combustibility (rate)		UL 94	v-2
Linear coefficient of thermal expansion	导热系数	JISR2618	0.2 W/m/K
specific heat	干		1670 J/(kg.k)
other	Test Condition	Test Method	ASAHI JAPAN/1300S
characteristic			标准.流动
hardness	Test Condition	Test Method	ASAHI JAPAN/1300S
Rockwell hardness		ASTM D785	120 M（Scale）
Basic Performance	Test Condition	Test Method	ASAHI JAPAN/1300S
Water absorption rate	湿		2.5 %
flammability	Test Condition	Test Method	ASAHI JAPAN/1300S
UL flame retardant rating		UL -94	V-2 0.40mm
Extreme Oxygen Index		ASTM2863	26 %
Electrical performance	Test Condition	Test Method	ASAHI JAPAN/1300S
Dissipation factor	相对漏电起痕指数	ASTM D3638	600 V
Volume resistivity		ASTM D257/IEC 60093	10-10 Ω.cm
Dielectric strength		ASTM D149	20 KV/mm
Other performance	Test Condition	Test Method	ASAHI JAPAN/1300S
Extreme Oxygen Index	干	ASTM D-2863	26 %