PC LUPOY® GP2101BF KA02 LG GUANGZHOU
176
- Unit Price:US$ 2,852 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜Glass fiber reinforced
- Application Areas:Laptop case
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 120 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | ASTM D648 | 230 °C | |
| melting temperature | ASTM D3418 | 260 °C | |
| Linear coefficient of thermal expansion | ASTM D696 | 3.0E-5 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 98.1 Mpa | |
| elongation | ASTM D638 | 3.0 % | |
| flexural modulus | ASTM D790 | 4900 Mpa | |
| bending strength | ASTM D790 | 142 Mpa |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | ASTM D955 | 0.70 - 1.2 % | |
| Water absorption rate | ASTM D570 | 0.70 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | ASTM D257 | 1.0E+14 ohms·cm | |
| dielectric strength | ASTM D149 | 22 KV/mm | |
| dielectric constant | ASTM D150 | 3.00 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 to 100 °C | ||
| drying time | 4.0 to 5.0 hr | ||
| Suggested maximum moisture content | 0.10 % | ||
| Temperature at the rear of the barrel | 265 to 275 °C | ||
| Temperature in the middle of the barrel | 270 to 280 °C | ||
| Temperature at the front of the material cylinder | 270 to 285 °C | ||
| Spray nozzle temperature | 270 to 280 °C | ||
| Processing (melt) temperature | 270 to 290 °C | ||
| mold temperature | 80 to 110 °C | ||
| Back pressure | 0.981 to 2.94 Mpa | ||
| screw speed | 60 to 150 rpm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.