PC GP2101BF KA02 LG GUANGZHOU

LUPOY®

Laptop case

Flame retardant,Glass fiber reinforced

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

hardness	Test Condition	Test Method	LG GUANGZHOU/GP2101BF KA02
Rockwell hardness	R-Scale, 23°C, Injection	ASTM D785	120

thermal performance	Test Condition	Test Method	LG GUANGZHOU/GP2101BF KA02
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm, Injection	ASTM D648	230 °C
Linear coefficient of thermal expansion	Flow	ASTM D696	3.0E-5 cm/cm/°C
Melting temperature		ASTM D3418	260 °C

mechanical properties	Test Condition	Test Method	LG GUANGZHOU/GP2101BF KA02
Bending modulus	23°C, 3.20 mm, Injection	ASTM D790	4900 Mpa
bending strength	23°C, 3.20 mm, Injection	ASTM D790	142 Mpa
elongation	Break, 23°C, 3.20 mm, Injection	ASTM D638	3.0 %
tensile strength	Yield, 23°C, 3.20 mm, Injection	ASTM D638	98.1 Mpa

Electrical performance	Test Condition	Test Method	LG GUANGZHOU/GP2101BF KA02
Compared to the anti leakage trace index	Solution A	IEC 60112	PLC 2
Dielectric constant	23°C, 1 MHz	ASTM D150	3.00
Dielectric strength	23°C, 1.00 mm	ASTM D149	22 KV/mm
Volume resistivity	23°C	ASTM D257	1.0E+14 ohms·cm

Physical properties	Test Condition	Test Method	LG GUANGZHOU/GP2101BF KA02
Shrinkage rate	23°C, 3.20 mm, Injection，Flow	ASTM D955	0.70 - 1.2 %
Water absorption rate	24 hr, 23°C	ASTM D570	0.70 %

flammability	Test Condition	Test Method	LG GUANGZHOU/GP2101BF KA02
UL flame retardant rating	0.8 mm	UL 94	V-0

injection	Test Condition	Test Method	LG GUANGZHOU/GP2101BF KA02
Back pressure			0.981 to 2.94 Mpa
drying temperature			80 to 100 °C
drying time			4.0 to 5.0 hr
Mold temperature			80 to 110 °C
Processing (melt) temperature			270 to 290 °C
Screw speed			60 to 150 rpm
Spray nozzle temperature			270 to 280 °C
Suggested maximum moisture content			0.10 %
Temperature at the front of the material cylinder			270 to 285 °C
Temperature at the rear of the barrel			265 to 275 °C
Temperature in the middle of the barrel			270 to 280 °C