PPS HZ1 SICHUAN DEYANG
196
- Unit Price:US$ 5,064 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:16MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant
- Application Areas:Home appliance components｜Automotive sector｜Electrical enclosure｜Mechanical components
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | GB/T 15585-1995 | 0.0025 mm/mm |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| purpose | 本品突出的特性及高性价比.在汽车、电子、电器、家电、机械、铁路等领域得-广泛应用 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | GB/T 1033-1986 | 2.1 g/cm³ |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation at break | ASTM D638/ISO 527 | 1.3 % | |
| tensile strength | ASTM D638/ISO 527 | 140(MPa) kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 110(HR) | |
| bending strength | ASTM D790/ISO 178 | 210(MPa) kg/cm²(MPa)[Lb/in²] | |
| compressive strength | GB/T 1041-1992 | 130 Mpa | |
| Rockwell hardness | GB/T 9342-1988 | 110 hr | |
| elongation | GB/T 1040-1992 | 1.3 % | |
| Flexural modulus | GB/T 1042-1992 | 1.8×104 Mpa | |
| bending strength | GB/T 1042-1992 | 210 Mpa | |
| Impact strength of cantilever beam gap | GB/T 1843-1996 | 6.5 kJ/m² | |
| tensile strength | GB/T 1040-1992 | 140 Mpa |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 2.1 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | GB/T 1409-1988 | 4 1MHz | |
| dielectric strength | GB/T 1408.1-1999 | 14 KV/mm | |
| Surface Resistivity | GB/T 1410-1989 | 2×1014 Ω | |
| Volume resistivity | GB/T 1410-1989 | 2×1014 Ω.m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | 282 ℃（℉） | ||
| GB/T 4608-1984 | 282 °C | ||
| Heat distortion temperature | GB/T 1634-1979 | 265 °C | |
| combustibility | GB/T 2408-1996 | FV-0 级 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.