Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS HZ1 SICHUAN DEYANG
--
Home appliance components、Automotive sector、Electrical enclosure、Mechanical components
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | SICHUAN DEYANG/HZ1 |
|---|---|---|---|
| density | GB/T 1033-1986 | 2.1 g/cm³ |
| Mechanical properties | Test Condition | Test Method | SICHUAN DEYANG/HZ1 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 210(MPa) kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | GB/T 9342-1988 | 110 hr | |
| bending strength | GB/T 1042-1992 | 210 Mpa | |
| Impact strength of cantilever beam gap | GB/T 1843-1996 | 6.5 kJ/m² | |
| compressive strength | GB/T 1041-1992 | 130 Mpa | |
| tensile strength | GB/T 1040-1992 | 140 Mpa | |
| elongation at break | ASTM D638/ISO 527 | 1.3 % | |
| Rockwell hardness | ASTM D785 | 110(HR) | |
| tensile strength | ASTM D638/ISO 527 | 140(MPa) kg/cm²(MPa)[Lb/in²] | |
| elongation | 断裂 | GB/T 1040-1992 | 1.3 % |
| Flexural modulus | GB/T 1042-1992 | 1.8×104 Mpa |
| Electrical performance | Test Condition | Test Method | SICHUAN DEYANG/HZ1 |
|---|---|---|---|
| Volume resistivity | GB/T 1410-1989 | 2×1014 Ω.m | |
| Surface Resistivity | GB/T 1410-1989 | 2×1014 Ω | |
| dielectric constant | GB/T 1409-1988 | 4 1MHz | |
| electric strength | GB/T 1408.1-1999 | 14 KV/mm |
| other | Test Condition | Test Method | SICHUAN DEYANG/HZ1 |
|---|---|---|---|
| purpose | 本品突出的特性及高性价比，在汽车、电子、电器、家电、机械、铁路等领域得到广泛应用 |
| Physical properties | Test Condition | Test Method | SICHUAN DEYANG/HZ1 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 2.1 |
| physical property | Test Condition | Test Method | SICHUAN DEYANG/HZ1 |
|---|---|---|---|
| Shrinkage rate | GB/T 15585-1995 | 0.0025 mm/mm |
| Thermal performance | Test Condition | Test Method | SICHUAN DEYANG/HZ1 |
|---|---|---|---|
| melting point | GB/T 4608-1984 | 282 °C | |
| combustibility | 垂直法 | GB/T 2408-1996 | FV-0 级 |
| melting point | 282 ℃（℉） | ||
| Heat distortion temperature | 1.80MPa | GB/T 1634-1979 | 265 °C |