PBT NOVADURAN™ 5010R8 MITSUBISHI ENGINEERING JAPAN

291

Unit Price:US$ 2,890 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
33MT
Delivery Terms:
FOB
Port of Loading :
Shenzhen Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜Flame retardant
Application Areas:Bottle cap｜Vehicle electronics
Color:--
Grade:Impact resistant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	>200	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.8mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	56.0	Mpa
Nominal tensile fracture strain		ISO 527-2	>200	%
Tensile strain	Yield	ISO 527-2	11	%
tensile strength	Yield	ISO 527-2	45.0	Mpa
Bending modulus		ISO 178	1650	Mpa
Tensile modulus		ISO 527-2	1550	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD：-30to50°C	ISO 11359-2	1.1E-04	cm/cm/°C
	Linear coefficient of thermal expansion	TD：50to120°C	ISO 11359-2	1.6E-04	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：50to120°C	ISO 11359-2	1.7E-04	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	155	°C
Linear coefficient of thermal expansion	MD：-30to50°C	ISO 11359-2	1.1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-30to120°C	ISO 11359-2	1.4E-04	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	70.0	°C
Melting temperature		ISO 11357-3	222	°C
Linear coefficient of thermal expansion	MD：-30to120°C	ISO 11359-2	1.4E-04	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	吸水率(Saturation,23°C)		0.090	%
	Shrinkage rate	MD:2.00mm		2.0	%
	Shrinkage rate	Shrinkage rate	TD:2.00mm		1.9	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	1MHz	IEC 60250	0.025
Relative permittivity	1MHz	IEC 60250	3.40
Dielectric strength	2.00mm	IEC 60243-1	17	KV/mm
Dielectric strength	Dielectric strength	1.00mm	IEC 60243-1	23	KV/mm
Surface resistivity		IEC 60093	4E+15	ohms
Volume resistivity		IEC 60093	1E+16	ohms·cm
Compared to the anti leakage trace index	CTI	UL 746	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Shenzhen Jufengde	US$ 2840 /MT

Supplier Join

Get App

Top

PBT NOVADURAN™ 5010R8 MITSUBISHI ENGINEERING JAPAN

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index