Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 5010R8 MITSUBISHI ENGINEERING JAPAN
NOVADURAN™ 
Bottle cap,Vehicle electronics
Glass fiber reinforced,Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

thermal performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/5010R8
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B155 °C
1.8MPa,UnannealedISO 75-2/A70.0 °C
Linear coefficient of thermal expansionTD：-30to50°CISO 11359-21.1E-04 cm/cm/°C
TD：-30to120°CISO 11359-21.4E-04 cm/cm/°C
MD：50to120°CISO 11359-21.7E-04 cm/cm/°C
MD：-30to120°CISO 11359-21.4E-04 cm/cm/°C
MD：-30to50°CISO 11359-21.1E-04 cm/cm/°C
TD：50to120°CISO 11359-21.6E-04 cm/cm/°C
Melting temperatureISO 11357-3222 °C
mechanical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/5010R8
Bending modulusISO 1781650 Mpa
bending strengthISO 17856.0 Mpa
Nominal tensile fracture strainISO 527-2>200 %
Tensile modulusISO 527-21550 Mpa
Tensile strainYieldISO 527-211 %
tensile strengthYieldISO 527-245.0 Mpa
Electrical performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/5010R8
Compared to the anti leakage trace indexCTIUL 746PLC 0
Dielectric strength2.00mmIEC 60243-117 KV/mm
1.00mmIEC 60243-123 KV/mm
Dissipation factor1MHzIEC 602500.025
Relative permittivity1MHzIEC 602503.40
Surface resistivityIEC 600934E+15 ohms
Volume resistivityIEC 600931E+16 ohms·cm
Physical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/5010R8
Shrinkage rateTD:2.00mm1.9 %
吸水率(Saturation,23°C)0.090 %
MD:2.00mm2.0 %
impact performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/5010R8
Impact strength of simply supported beam without notch23°CISO 179>200 kJ/m²
flammabilityTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/5010R8
UL flame retardant rating0.8mmUL 94HB