thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45MPa,未退火,6.40mm	ASTM D648	154 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,未退火,6.40mm	ASTM D648	54.4 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	8.1E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：60to138°C	ASTME831	1.4E-04 cm/cm/°C

Impact resistance	Test Condition	Test Method	Test Result
GardnerImpact	23°C	ASTM D3029	40.7 J

Physical properties	Test Condition	Test Method	Test Result
melt viscosity		内部方法	110 Pa·s
Specific volume		ASTM D792	0.770 cm³/g
shrinkage rate	MD：--2	内部方法	0.90-1.6 %
	shrinkage rate	MD：--3	内部方法	1.5-2.3 %
		shrinkage rate	TD：--2	内部方法	1.0-1.7 %
		shrinkage rate	shrinkage rate	TD：--3	内部方法	1.6-2.4 %
Water absorption rate	24hr	ASTM D570	0.080 %

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	屈服	ASTM D638	51.7 Mpa
elongation	断裂	ASTM D638	10 %
flexural modulus	50.0mmSpan	ASTM D790	2340 Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	82.7 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.