Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 215HPR-1001 SABIC INNOVATIVE US
VALOX™
Home appliance components,Automotive Applications
High rigidity,high strength
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/215HPR-1001 |
|---|---|---|---|
| GardnerImpact | 23°C | ASTM D3029 | 40.7 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/215HPR-1001 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 10 % |
| bending strength | Yield,50.0mmSpan | ASTM D790 | 82.7 Mpa |
| Flexural modulus | 50.0mmSpan | ASTM D790 | 2340 Mpa |
| tensile strength | 屈服 | ASTM D638 | 51.7 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/215HPR-1001 |
|---|---|---|---|
| Shrinkage rate | TD：--2 | 内部方法 | 1.0-1.7 % |
| TD：--3 | 内部方法 | 1.6-2.4 % | |
| Water absorption rate | 24hr | ASTM D570 | 0.080 % |
| Shrinkage rate | MD：--2 | 内部方法 | 0.90-1.6 % |
| Specific volume | ASTM D792 | 0.770 cm³/g | |
| Shrinkage rate | MD：--3 | 内部方法 | 1.5-2.3 % |
| melt viscosity | 内部方法 | 110 Pa·s |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/215HPR-1001 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 54.4 °C |
| Linear coefficient of thermal expansion | MD：60to138°C | ASTME831 | 1.4E-04 cm/cm/°C |
| MD：-40to40°C | ASTME831 | 8.1E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 154 °C |