PA66 Leona™ 54G43 NC ASAHI JAPAN
200
- Unit Price:US$ 4,003 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:75.7MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:high strength｜High rigidity｜Filler: Glass fiber reinforced material｜Enhanced strength｜Rigidity and impact resistance｜43% filler by weight｜Glass fiber content is 43%｜Good appearance
- Application Areas:Automotive Applications｜Gears｜Application in the automotive field｜component｜Industrial applications｜Fabric｜Fan｜Railway sleeper insulation｜Office Furniture
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 93 |
| R计秤 | ASTM D785 | 118 | |
| M计秤 | ISO 2039-2 | 93 | |
| R计秤 | ISO 2039-2 | 118 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.46MPa,干 | ASTM D-648 | 250 °C |
| 1.82MPa,干 | ASTM D-648 | 240 °C | |
| UL flame retardant rating | 干 | UL 94 | HB |
| Heat Deflection Temperature | 0.45MPa,未退火 | ASTM D648 | 250 °C |
| 0.45MPa,未退火 | ISO 75-2/B | 245 °C | |
| 1.8MPa,未退火 | ASTM D648 | 240 °C | |
| 1.8MPa,未退火 | ISO 75-2/A | 230 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 湿 | 1.6 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 99 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | 干 | 旭化成方法 | 0.3/0.7 % |
| TD | 内部方法 | 0.70 % | |
| MD | 内部方法 | 0.30 % | |
| 吸水率(饱和,23°C) | 内部方法 | -- % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | -- % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1E+15 ohms | |
| IEC 60093 | 1E+15 ohms | ||
| volume resistivity | ASTM D257 | 1E+15 ohms·cm | |
| 23°C | IEC 60093 | 1E+15 ohms·cm | |
| dielectric strength | ASTM D149 | 32 KV/mm | |
| IEC 60243-1 | 32 KV/mm | ||
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | IEC 60112 | PLC 0 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 干(湿) | ASTM D-638 | 186(132) Mpa |
| bending strength | 干(湿) | ASTM D-790 | 304(177) Mpa |
| Rockwell hardness | 干(湿) | ASTM D-785 | 118(-) R scale |
| flexural coefficient | 干(湿) | ASTM D-790 | 11.0(5.9) GPa |
| Impact strength of cantilever beam gap | 干(湿) | ASTM D-256 | 147(226) J/m |
| Rockwell hardness | 干(湿) | ASTM D-785 | 93(-) M Scale |
| Elongation at break | 干(湿) | ASTM D-638 | 3(4) % |
| Tensile modulus | 23°C | ISO 527-2 | 12200 Mpa |
| tensile strength | ASTM D638 | 186 Mpa | |
| 断裂,23°C | ISO 527-2 | 200 Mpa | |
| elongation | 断裂 | ASTM D638 | 3.0 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | 4.0 % |
| flexural modulus | ASTM D790 | 11000 Mpa | |
| 23°C | ISO 178 | 10600 Mpa | |
| bending strength | ASTM D790 | 304 Mpa | |
| 23°C | ISO 178 | 290 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.