Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 54G43 NC ASAHI JAPAN
Leona™
Automotive Applications,Gears,Application in the automotive field,component,Industrial applications,Fabric,Fan,Railway sleeper insulation,Office Furniture
high strength,High rigidity,Filler: Glass fiber reinf,Enhanced strength,Rigidity and impact resis,43% filler by weight,Glass fiber content is 43,Good appearance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ASAHI JAPAN/54G43 NC |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 99 kJ/m² |
| hardness | Test Condition | Test Method | ASAHI JAPAN/54G43 NC |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 93 |
| R计秤 | ISO 2039-2 | 118 | |
| M计秤 | ISO 2039-2 | 93 | |
| R计秤 | ASTM D785 | 118 |
| Basic performance | Test Condition | Test Method | ASAHI JAPAN/54G43 NC |
|---|---|---|---|
| Water absorption rate | 湿 | 1.6 % |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/54G43 NC |
|---|---|---|---|
| Impact strength of cantilever beam gap | 干(湿) | ASTM D-256 | 147(226) J/m |
| flexural coefficient | 干(湿) | ASTM D-790 | 11.0(5.9) GPa |
| bending strength | ASTM D790 | 304 Mpa | |
| tensile strength | 干(湿) | ASTM D-638 | 186(132) Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 12200 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 200 Mpa |
| Flexural modulus | ASTM D790 | 11000 Mpa | |
| tensile strength | ASTM D638 | 186 Mpa | |
| Rockwell hardness | 干(湿) | ASTM D-785 | 118(-) R scale |
| 干(湿) | ASTM D-785 | 93(-) M Scale | |
| elongation | 断裂 | ASTM D638 | 3.0 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | 4.0 % |
| bending strength | 23°C | ISO 178 | 290 Mpa |
| 干(湿) | ASTM D-790 | 304(177) Mpa | |
| Flexural modulus | 23°C | ISO 178 | 10600 Mpa |
| elongation at break | 干(湿) | ASTM D-638 | 3(4) % |
| Electrical performance | Test Condition | Test Method | ASAHI JAPAN/54G43 NC |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | IEC 60112 | PLC 0 |
| Volume resistivity | ASTM D257 | 1E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 32 KV/mm | |
| Surface Resistivity | ASTM D257 | 1E+15 ohms | |
| Volume resistivity | 23°C | IEC 60093 | 1E+15 ohms·cm |
| dielectric strength | ASTM D149 | 32 KV/mm | |
| Surface Resistivity | IEC 60093 | 1E+15 ohms |
| flammability | Test Condition | Test Method | ASAHI JAPAN/54G43 NC |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| physical property | Test Condition | Test Method | ASAHI JAPAN/54G43 NC |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.30 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | -- % |
| Shrinkage rate | 吸水率(饱和,23°C) | 内部方法 | -- % |
| TD | 内部方法 | 0.70 % | |
| 干 | 旭化成方法 | 0.3/0.7 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/54G43 NC |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 240 °C |
| 1.82MPa,干，HDT | ASTM D-648 | 240 °C | |
| 0.45MPa,未退火，HDT | ASTM D648 | 250 °C | |
| 0.46MPa,干，HDT | ASTM D-648 | 250 °C | |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 245 °C | |
| UL flame retardant rating | 干 | UL 94 | HB |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 230 °C |