PA66

PA66 Leona™ 1500 ASAHI JAPAN

231

Unit Price:US$ 4,165 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
83.8MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:high molecular weight
Application Areas:Fasteners｜PA board
Color:--
Grade:Injection grade

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			高粘度

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179	NoBreak

Basic Performance	Test Condition	Test Method	Test Result
Water absorption rate	湿		2.5 %

mechanical properties	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ASTM D256/ISO 179	49 kg·cm/cm(J/M)ft·lb/in
Rockwell hardness		ASTM D785	R120
Bending modulus		ASTM D790/ISO 178	2790 kg·cm/cm(J/M)ft·lb/in
bending strength		ASTM D790/ISO 178	118 kg·cm/cm(J/M)ft·lb/in
flexural coefficient	干(湿)	ASTM D-790	2.8(1.2) GPa
Impact strength of cantilever beam gap	干(湿)	ASTM D-256	49(176) J/m
Rockwell hardness	干(湿)	ASTM D-785	80(55) M Scale
tensile strength	干(湿)	ASTM D-638	79(57) Mpa
Rockwell hardness	干(湿)	ASTM D-785	120(105) R scale
Elongation at Break	干(湿)	ASTM D-638	80(270) %
bending strength	干(湿)	ASTM D-790	118(54) Mpa
Tensile modulus	23°C	ISO 527-2	2900 Mpa
tensile strength		ASTM D638	79.0 Mpa
tensile strength	tensile strength	Yield,23°C	ISO 527-2	84.0 Mpa
Tensile strain	Yield,23°C	ISO 527-2	4.5 %
elongation	Break	ASTM D638	80 %
Tensile strain	Break,23°C	ISO 527-2	-- %
Bending modulus		ASTM D790	2800 Mpa
Bending modulus	Bending modulus	23°C	ISO 178	2700 Mpa
bending strength		ASTM D790	118 Mpa
bending strength	bending strength	23°C	ISO 178	110 Mpa
Taber abraser	1000Cycles	ASTM D1044	-- mg

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	HDT	ASTM D648/ISO 75	230 ℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	8 mm/mm.℃
thermal conductivity	干		0.2 W/(m.K)
specific heat	干		1670 J/(kg.k)
Hot deformation temperature	0.46MPa,干	ASTM D-648	230 °C
Linear coefficient of thermal expansion	干	ASTM D-696	8
Hot deformation temperature	1.82MPa,干	ASTM D-648	70 °C
	Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	230 °C
		Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	195 °C
			Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	70.0 °C
			Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	65.0 °C
Linear coefficient of thermal expansion	MD	ASTM D696	8E-05 cm/cm/°C
specific heat			1670 J/kg/°C
thermal conductivity			0.20 W/m/K

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	1.14
Water absorption rate		ASTM D570/ISO 62	2.5 %
Shrinkage rate	干	旭化成方法	1.3-2.0 %
Wear factor	湿	ASTM D-1044	5
Shrinkage rate	MD	Internal Method	1.3-2.0 %
Water absorption rate	Saturation,23°C		-- %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	-- %

Electrical performance	Test Condition	Test Method	Test Result
Dielectric strength		IEC 60243-1	20 KV/mm
Compared to the anti leakage trace index	3.00mm	IEC 60112	PLC 0
Surface resistivity		ASTM D257	1E+14 ohms
Surface resistivity	Surface resistivity		IEC 60093	1E+14 ohms
Volume resistivity		ASTM D257	1E+15 ohms·cm
Volume resistivity	Volume resistivity	23°C	IEC 60093	1E+15 ohms·cm
Dielectric strength		ASTM D149	20 KV/mm

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Sale	ASTM D785	80
	Rockwell hardness	R-Sale	ASTM D785	120
		Rockwell hardness	M-Sale	ISO 2039-2	80
		Rockwell hardness	Rockwell hardness	R-Sale	ISO 2039-2	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 Leona™ 1500 ASAHI JAPAN

Material Description

Technical Data Sheet Compare

Technical Data Sheet