PA66 Leona™ 1402S ASAHI JAPAN
338
- Unit Price:US$ 4,210 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:105MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜Thermal stability｜Fatigue resistance｜high strength｜High rigidity
- Application Areas:Automotive sector｜Laptop case｜Consumer goods sector｜Wire and cable applications
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 80 |
| R计秤 | ASTM D785 | 120 | |
| M计秤 | ISO 2039-2 | 80 | |
| R计秤 | ISO 2039-2 | 120 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | 干 | ASTM D-696 | 8 |
| specific heat | 干 | 1670 J/(kg.k) | |
| UL flame retardant rating | 干 | UL 94 | V-2 |
| Heat Deflection Temperature | 0.46MPa,干 | ASTM D-648 | 230 °C |
| thermal conductivity | 干 | 0.2 W/(m.K) | |
| Heat Deflection Temperature | 1.82MPa,干 | ASTM D-648 | 70 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 70.0 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 8E-05 cm/cm/°C |
| specific heat | 1670 J/kg/°C | ||
| thermal conductivity | 0.20 W/m/K | ||
| Heat Deflection Temperature | 0.45MPa,未退火 | ASTM D648 | 230 °C |
| 0.45MPa,未退火 | ISO 75-2/B | 190 °C | |
| 1.8MPa,未退火 | ASTM D648 | 70.0 °C | |
| Combustibility (rate) | UL 94 | v-2 | |
| Heat Deflection Temperature | HDT | ASTM D648/ISO 75 | 230 ℃（℉） |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 8 mm/mm.℃ |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 耐热 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-2 |
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
| Limiting Oxygen Index | ASTM D2863 | 26 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 湿 | 2.5 % |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Limiting Oxygen Index | 干 | ASTM D-2863 | 26 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | NoBreak |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Wear factor | 湿 | ASTM D-1044 | 7 |
| shrinkage rate | 干 | 旭化成方法 | 1.3-2.0 % |
| MD | 内部方法 | 1.3-2.0 % | |
| Water absorption rate | 饱和,23°C | -- % | |
| 平衡,23°C,50%RH | ISO 62 | -- % | |
| density | ASTM D792/ISO 1183 | 1.14 | |
| shrinkage rate | ASTM D955 | 1.3-2.0 % | |
| Water absorption rate | ASTM D570/ISO 62 | 2.5 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | IEC 60112 | PLC 1 |
| Surface Resistivity | ASTM D257 | 1E+13 ohms | |
| IEC 60093 | 1E+13 ohms | ||
| volume resistivity | ASTM D257 | 1E+14 ohms·cm | |
| 23°C | IEC 60093 | 1E+14 ohms·cm | |
| dielectric strength | ASTM D149 | 20 KV/mm | |
| IEC 60243-1 | 20 KV/mm | ||
| volume resistivity | ASTM D257/IEC 60093 | 10.10 Ω.cm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | 干(湿) | ASTM D-785 | 80(55) M Scale |
| 干(湿) | ASTM D-785 | 120(108) R scale | |
| Impact strength of cantilever beam gap | 干(湿) | ASTM D-256 | 39(147) J/m |
| bending strength | 干(湿) | ASTM D-790 | 118(54) Mpa |
| flexural coefficient | 干(湿) | ASTM D-790 | 2.8(1.2) GPa |
| tensile strength | 干(湿) | ASTM D-638 | 79(57) Mpa |
| Elongation at break | 干(湿) | ASTM D-638 | 50(250) % |
| Tensile modulus | 23°C | ISO 527-2 | 3000 Mpa |
| tensile strength | ASTM D638 | 79.0 Mpa | |
| 屈服,23°C | ISO 527-2 | 82.0 Mpa | |
| Tensile strain | 屈服,23°C | ISO 527-2 | 4.0 % |
| elongation | 断裂 | ASTM D638 | 50 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | -- % |
| flexural modulus | ASTM D790 | 2800 Mpa | |
| 23°C | ISO 178 | 2700 Mpa | |
| bending strength | ASTM D790 | 118 Mpa | |
| 23°C | ISO 178 | 113 Mpa | |
| Taber abraser | 1000Cycles | ASTM D1044 | -- mg |
| Elongation at break | ASTM D638/ISO 527 | 50 % | |
| elongation | ASTM D638/ISO 527 | 78.5 % | |
| flexural modulus | ASTM D790/ISO 178 | 2790 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 118 kg·cm/cm(J/M)ft·lb/in | |
| Elongation at break | ASTM D638/ISO 527 | - % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.