Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 1402S ASAHI JAPAN
Leona™
Automotive sector,Laptop case,Consumer goods sector,Wire and cable applications
Flame retardant,Thermal stability,Fatigue resistance,high strength,High rigidity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | ASAHI JAPAN/1402S |
|---|---|---|---|
| Limiting Oxygen Index | 干 | ASTM D-2863 | 26 % |
| Impact resistance | Test Condition | Test Method | ASAHI JAPAN/1402S |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | NoBreak |
| hardness | Test Condition | Test Method | ASAHI JAPAN/1402S |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 80 |
| R计秤 | ISO 2039-2 | 120 | |
| M计秤 | ISO 2039-2 | 80 | |
| R计秤 | ASTM D785 | 120 |
| Basic performance | Test Condition | Test Method | ASAHI JAPAN/1402S |
|---|---|---|---|
| Water absorption rate | 湿 | 2.5 % |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/1402S |
|---|---|---|---|
| Impact strength of cantilever beam gap | 干(湿) | ASTM D-256 | 39(147) J/m |
| flexural coefficient | 干(湿) | ASTM D-790 | 2.8(1.2) GPa |
| bending strength | ASTM D790 | 118 Mpa | |
| elongation | ASTM D638/ISO 527 | 78.5 % | |
| tensile strength | 干(湿) | ASTM D-638 | 79(57) Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 3000 Mpa |
| Flexural modulus | ASTM D790/ISO 178 | 2790 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 118 kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | - % | |
| Flexural modulus | ASTM D790 | 2800 Mpa | |
| tensile strength | ASTM D638 | 79.0 Mpa | |
| Taber abraser | 1000Cycles | ASTM D1044 | -- mg |
| Rockwell hardness | 干(湿) | ASTM D-785 | 120(108) R scale |
| 干(湿) | ASTM D-785 | 80(55) M Scale | |
| elongation | 断裂 | ASTM D638 | 50 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | -- % |
| bending strength | 23°C | ISO 178 | 113 Mpa |
| 干(湿) | ASTM D-790 | 118(54) Mpa | |
| tensile strength | 屈服,23°C | ISO 527-2 | 82.0 Mpa |
| Tensile strain | 屈服,23°C | ISO 527-2 | 4.0 % |
| Flexural modulus | 23°C | ISO 178 | 2700 Mpa |
| elongation at break | 干(湿) | ASTM D-638 | 50(250) % |
| Electrical performance | Test Condition | Test Method | ASAHI JAPAN/1402S |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | IEC 60112 | PLC 1 |
| Volume resistivity | ASTM D257 | 1E+14 ohms·cm | |
| dielectric strength | IEC 60243-1 | 20 KV/mm | |
| Surface Resistivity | ASTM D257 | 1E+13 ohms | |
| Volume resistivity | 23°C | IEC 60093 | 1E+14 ohms·cm |
| dielectric strength | ASTM D149 | 20 KV/mm | |
| Surface Resistivity | IEC 60093 | 1E+13 ohms | |
| Volume resistivity | ASTM D257/IEC 60093 | 10.10 Ω.cm |
| other | Test Condition | Test Method | ASAHI JAPAN/1402S |
|---|---|---|---|
| characteristic | 耐热 |
| Physical properties | Test Condition | Test Method | ASAHI JAPAN/1402S |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 1.3-2.0 % | |
| density | ASTM D792/ISO 1183 | 1.14 | |
| Water absorption rate | ASTM D570/ISO 62 | 2.5 % |
| flammability | Test Condition | Test Method | ASAHI JAPAN/1402S |
|---|---|---|---|
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 0.75mm | UL 94 | V-2 |
| Limiting Oxygen Index | ASTM D2863 | 26 % |
| physical property | Test Condition | Test Method | ASAHI JAPAN/1402S |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 1.3-2.0 % |
| Water absorption rate | 饱和,23°C | -- % | |
| 平衡,23°C,50%RH | ISO 62 | -- % | |
| Wear factor | 湿 | ASTM D-1044 | 7 |
| Shrinkage rate | 干 | 旭化成方法 | 1.3-2.0 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/1402S |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 70.0 °C |
| Combustibility (rate) | UL 94 | v-2 | |
| specific heat | 干 | 1670 J/(kg.k) | |
| Linear coefficient of thermal expansion | 干 | ASTM D-696 | 8 |
| ASTM D696/ISO 11359 | 8 mm/mm.℃ | ||
| Heat distortion temperature | 1.82MPa,干，HDT | ASTM D-648 | 70 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 230 °C | |
| thermal conductivity | 0.20 W/m/K | ||
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 230 ℃（℉） |
| 0.46MPa,干，HDT | ASTM D-648 | 230 °C | |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 190 °C | |
| thermal conductivity | 干 | 0.2 W/(m.K) | |
| UL flame retardant rating | 干 | UL 94 | V-2 |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 70.0 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 8E-05 cm/cm/°C |
| specific heat | 1670 J/kg/°C |