PC LEXAN™ ML7694-739 SABIC INNOVATIVE NANSHA
195
- Unit Price:US$ 2,806 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:23.8MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Middle flow｜Fatigue resistance｜Filler: Glass fiber reinforced material｜10% filler by weight
- Application Areas:Electronic and electrical accessories｜Home appliance products
- Color:--
- Grade:Light diffusion level
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTM D648 | 146 °C |
| 1.8MPa,未退火,6.40mm | ASTM D648 | 142 °C | |
| vicat | ASTM D15257 | 154 °C | |
| Linear coefficient of thermal expansion | MD：-40到95°C | ASTME831 | 3.2E-05 cm/cm/°C |
| thermal conductivity | ASTMC177 | 0.20 W/m/K | |
| RTI Elec | UL 746 | 120 °C | |
| RTI Imp | UL 746 | 110 °C | |
| RTI | UL 746 | 125 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.52mm | UL 94 | V-0 |
| 2.99mm | UL 94 | 5VA |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 23°C | ASTM D256 | 100 J/m | |
| -30°C | ISO 180/1A | 9.0 kJ/m² | |
| 23°C | ISO 180/1A | 10 kJ/m² | |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 2100 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| High arc combustion index (HAI) | HAI | UL 746 | PLC 1 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 1 |
| volume resistivity | ASTM D257 | >1.0E+17 ohms·cm | |
| dielectric strength | 3.20mm,inAir | ASTM D149 | 18 KV/mm |
| arc resistance | ASTM D495 | PLC7 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 4 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Specific volume | ASTM D792 | 0.800 cm³/g | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 7.5 g/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.20-0.40 % |
| Water absorption rate | 平衡,23°C | ASTM D570 | 0.31 % |
| Outdoor applicability | UL 746C | f1 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 断裂 | ASTM D638 | 53.0 Mpa |
| elongation | 断裂 | ASTM D638 | 15 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 3440 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 100 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.