PC ML7694-739 SABIC INNOVATIVE NANSHA
LEXAN™
Electronic and electrical、Home appliance products
Middle flow、Fatigue resistance、Filler: Glass fiber reinf、10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/ML7694-739 |
|---|---|---|---|
| 23°C | ISO 180/1A | 10 kJ/m² | |
| ASTM D256 | 100 J/m | ||
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 2100 J/m |
| -30°C | ISO 180/1A | 9.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/ML7694-739 |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| Volume resistivity | ASTM D257 | >1.0E+17 ohms·cm | |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 1 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 1 |
| arc resistance | ASTM D495 | PLC7 | |
| dielectric strength | 3.20mm,inAir | ASTM D149 | 18 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 4 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/ML7694-739 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 15 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 100 Mpa |
| tensile strength | 断裂 | ASTM D638 | 53.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 3440 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/ML7694-739 |
|---|---|---|---|
| UL flame retardant rating | 1.52mm | UL 94 | V-0 |
| 2.99mm | UL 94 | 5VA |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/ML7694-739 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.20-0.40 % |
| Outdoor applicability | UL 746C | f1 | |
| Water absorption rate | 平衡,23°C | ASTM D570 | 0.31 % |
| Specific volume | ASTM D792 | 0.800 cm³/g | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 7.5 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/ML7694-739 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 142 °C |
| thermal conductivity | ASTMC177 | 0.20 W/m/K | |
| Linear coefficient of thermal expansion | MD：-40到95°C | ASTME831 | 3.2E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 146 °C |
| RTI Imp | UL 746 | 110 °C | |
| RTI | UL 746 | 125 °C | |
| vicat | ASTM D15257 | 154 °C | |
| RTI Elec | UL 746 | 120 °C |