PA66 Zytel® 70G33HS1L BK031 DUPONT SHENZHEN
333
- Unit Price:US$ 3,193 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:150.8MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
- Material Comparison:PA66 Zytel® 70G33HS1L BK031 DUPONT USA
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Thermal stability｜high strength｜Glass fiber reinforced
- Application Areas:Automotive sector
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 261 °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 252 °C | |
| melting temperature | ISO 11357-3 | 262 °C | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 1.8E-5 cm/cm/°C |
| 流动 : -40 到 23°C | ISO 11359-2 | 2.4E-5 cm/cm/°C | |
| 流动 : 55 到 160°C | ISO 11359-2 | 1.3E-5 cm/cm/°C | |
| 横向 | ISO 11359-2 | 8.3E-5 cm/cm/°C | |
| 横向 : -40 到 23°C | ISO 11359-2 | 6.5E-5 cm/cm/°C | |
| 横向 : 55 到 160°C | ISO 11359-2 | 1.4E-4 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | 1.00 mm | ISO 3795 | 28 mm/min |
| UL flame retardant rating | UL 94 | HB | |
| UL 94 | HB | ||
| FMVSS combustion rate | FMVSS 302 | B | |
| 雾化 - G-value (condensate) | ISO 6452 | 6.0E-4 g |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 75 kJ/m² |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Ejection Temperature | 210 °C | ||
| Emission of Organic Compounds | VDA 277 | 10.0 µgC/g | |
| Odor | VDA 270 | 3.00 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | 横向流量 | ISO 294-4 | 1.1 % |
| 流量 | ISO 294-4 | 0.30 % | |
| Water absorption rate | 饱和, 23°C, 2.00 mm | ISO 62 | 5.7 % |
| 平衡, 23°C, 2.00 mm, 50% RH | ISO 62 | 1.8 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 1 | |
| IEC 60112 | PLC 1 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 °C | ||
| Drying time - hot air dryer | 2.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.20 % | ||
| Processing (melt) temperature | 275 to 295 °C | ||
| Melt Temperature, Optimum | 285 °C | ||
| mold temperature | 70 to 120 °C | ||
| Mold Temperature, Optimum | 100 °C | ||
| pressure holding | 50.0 to 100 Mpa | ||
| Drying Recommended | yes | ||
| Hold Pressure Time | 3.00 s/mm | ||
| Maximum Screw Tangential Speed | 12 m/min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 11000 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 200 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 3.0 % |
| flexural modulus | ISO 178 | 9500 Mpa | |
| bending strength | ISO 178 | 280 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.