PA66 70G33HS1L BK031 DUPONT SHENZHEN
Zytel® 
Automotive sector
Thermal stability,high strength,Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

thermal performanceTest ConditionTest MethodDUPONT SHENZHEN/70G33HS1L BK031
Hot deformation temperature0.45 MPa, UnannealedISO 75-2/B261 °C
1.8 MPa, UnannealedISO 75-2/A252 °C
Linear coefficient of thermal expansionAcross Flow : 55 to 160°CISO 11359-21.4E-4 cm/cm/°C
Flow : -40 to 23°CISO 11359-22.4E-5 cm/cm/°C
Across FlowISO 11359-28.3E-5 cm/cm/°C
FlowISO 11359-21.8E-5 cm/cm/°C
Flow : 55 to 160°CISO 11359-21.3E-5 cm/cm/°C
Across Flow : -40 to 23°CISO 11359-26.5E-5 cm/cm/°C
Melting temperatureISO 11357-3262 °C
mechanical propertiesTest ConditionTest MethodDUPONT SHENZHEN/70G33HS1L BK031
Bending modulusISO 1789500 Mpa
bending strengthISO 178280 Mpa
Tensile modulusISO 527-211000 Mpa
Tensile strainBreakISO 527-23.0 %
tensile strengthBreakISO 527-2200 Mpa
Electrical performanceTest ConditionTest MethodDUPONT SHENZHEN/70G33HS1L BK031
Compared to the anti leakage trace indexIEC 60112PLC 1
UL 746PLC 1
Physical propertiesTest ConditionTest MethodDUPONT SHENZHEN/70G33HS1L BK031
Shrinkage rate横向FlowISO 294-41.1 %
FlowISO 294-40.30 %
Water absorption rateSaturation, 23°C, 2.00 mmISO 625.7 %
Equilibrium, 23°C, 2.00 mm, 50% RHISO 621.8 %
impact performanceTest ConditionTest MethodDUPONT SHENZHEN/70G33HS1L BK031
Impact strength of simply supported beam without notch23°CISO 179/1eU75 kJ/m²
flammabilityTest ConditionTest MethodDUPONT SHENZHEN/70G33HS1L BK031
Burning rate1.00 mmISO 379528 mm/min
FMVSS combustion rateFMVSS 302B
UL flame retardant ratingUL 94HB
雾化 - G-value (condensate)ISO 64526.0E-4 g
Filling analysisTest ConditionTest MethodDUPONT SHENZHEN/70G33HS1L BK031
Emission of Organic CompoundsVDA 27710.0 µgC/g
OdorVDA 2703.00
Top out temperature210 °C
injectionTest ConditionTest MethodDUPONT SHENZHEN/70G33HS1L BK031
drying temperature80 °C
Drying time - hot air dryer2.0 to 4.0 hr
Hold Pressure Time3.00 s/mm
Maintain pressureDrying Recommendedyes
50.0 to 100 Mpa
Maximum Screw Tangential Speed12 m/min
Melt Temperature, Optimum285 °C
Mold temperature70 to 120 °C
Mold Temperature, Optimum100 °C
Processing (melt) temperature275 to 295 °C
Suggested maximum moisture content0.20 %